| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL STN15HF PPE+PS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Automotive interiors. Improved flow characteristics/overall processing economy. 240F DTUL. High impact/good property retention after heat ageing.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Water Absorption | 0.20 % @Time 86400 sec |
0.20 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 46.0 MPa | 6670 psi | Type I, 50 mm/min; ASTM D638 |
| Elongation at Break | 70 % | 70 % | Type I, 50 mm/min; ASTM D638 |
| Flexural Yield Strength | 69.0 MPa | 10000 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Flexural Modulus | 1.99 GPa | 289 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Izod Impact, Notched | 4.53 J/cm | 8.49 ft-lb/in | ASTM D256 |
| 2.24 J/cm @Temperature -40.0 °C |
4.20 ft-lb/in @Temperature -40.0 °F |
ASTM D256 | |
| 2.50 J/cm @Temperature -20.0 °C |
4.68 ft-lb/in @Temperature -4.00 °F |
ASTM D256 | |
| Dart Drop, Total Energy | 36.0 J | 26.6 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| 24.0 J @Temperature -30.0 °C |
17.7 ft-lb @Temperature -22.0 °F |
Instrumented Impact Energy @ peak; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 117 µm/m-°C @Temperature 0.000 - 100 °C |
65.0 µin/in-°F @Temperature 32.0 - 212 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C @Thickness 6.40 mm |
244 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 115 °C @Thickness 6.40 mm |
239 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Pyrotek EZ-400 Refractory Coating
- Lehmann & Voss LUVOCOM® 50/TF/15/NAT Polycarbonate, with PTFE, easy flowing
- A. Schulman LP552-01 Narrow Molecular Weight Copolymer, High-Density Polyethylene
- Zig Sheng Industrial ZISAMIDE® TP6802 Nylon 6
- Borealis Borstar® MB7542 High Density Polyethylene for Injection Molding
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, Hardness 40A, Non-Black Sulfur Cure
- Chesterton ARC BX2 Contractor Grade Fine Sliding Wear Compound
- ExxonMobil Exxon™ 365 Low Mooney Grade
- BNZ Materials Bazelite 2300 LI Insulating Castable
- DuPont Performance Polymers Hytrel® 4556 TPC-ET (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved