SABIC Innovative Plastics NORYL PX0844 PPE+HIPS (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL PX0844 PPE+HIPS (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
NORYL PX0844 is an unfilled standard material with a Vicat B/120 of 125°C according ISO306. NORYL PX0844 offers high heat resistance and consistant processability. Typical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.0300 % | 0.0300 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.14 % | 0.14 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | on Tensile Bar; SABIC Method |
| Melt Index of Compound | 9.0 g/10 min @Load 3.80 kg, Temperature 280 °C |
9.0 g/10 min @Load 8.38 lb, Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 35.0 MPa | 5080 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 40 % | 40 % | 50 mm/min; ISO 527 |
| Elongation at Yield | 4.0 % | 4.0 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 2.30 GPa | 334 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 65.0 MPa | 9430 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.20 GPa | 319 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*4; ISO 180/1A |
| 5.00 kJ/m² @Temperature -40.0 °C |
2.38 ft-lb/in² @Temperature -40.0 °F |
80*10*4; ISO 180/1A | |
| 7.00 kJ/m² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 80.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
44.4 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
50.0 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 |
| Thermal Conductivity | 0.230 W/m-K | 1.60 BTU-in/hr-ft²-°F | ISO 8302 |
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| Vicat Softening Point | 123 °C | 253 °F | Rate B/50; ISO 306 |
| 125 °C | 257 °F | Rate B/120; ISO 306 | |
| 130 °C | 266 °F | Rate A/50; ISO 306 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 75°C +/- 2°C | PASSES | IEC 60695-10-2 |
Users viewing this material also viewed the following:
- I. Stern N2560 General Purpose Crystal Polystyrene
- Kingfa LONOY 1200 PC/PBT Alloy
- Kolon KOCETAL® K300EW Standard Grade Acetal Resin
- Momentive Performance Materials Siloprenâ„¢ LSR 2645 Custom Liquid Silicone Rubber - Infant Care
- Michelman® Michem® Guard 349 Nonionic, polyethylene dispersion
- DuPont Elvax® 3165 Ethylene-Vinyl Acetate Copolymer Resin for Coextrusion, Blown Film
- Barlog Plastics KEBATRON L2040G3 PPS, linear, 40% glass fiber reinforced, reduced residual chlorine
- Arlon CP-PC-2951 Silicone Compound
- 3M 436 Vibration Damping Tape
Copyright © lookpolymers.com All Rights Reserved