SABIC Innovative Plastics NORYL PCN2615H PPE+PS (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL PCN2615H PPE+PS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PPE+PS, Noryl, Glass Fiber, Mica, Flame Retardant, UL Grade, Non-Halogen Flame Retaardant, High Flow,
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.39 g/cc | 1.39 g/cc | ASTM D792 |
| Melt Flow | 13.4 g/10 min @Load 2.16 kg, Temperature 300 °C |
13.4 g/10 min @Load 4.76 lb, Temperature 572 °F |
ASTM D1238 |
| Spiral Flow | 655 cm @Thickness 3.00 mm |
258 in @Thickness 0.118 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 97.0 MPa | 14100 psi | Type I, 10 mm/min; SABIC - Japan Method |
| Tensile Strength, Yield | 97.0 MPa | 14100 psi | Type I, 10 mm/min; SABIC - Japan Method |
| Elongation at Break | 6.0 % | 6.0 % | Type I, 10 mm/min; SABIC - Japan Method |
| Elongation at Yield | 6.0 % | 6.0 % | Type I, 10 mm/min; SABIC - Japan Method |
| Flexural Strength | 141 MPa | 20500 psi | ASTM D790 |
| Flexural Modulus | 8.40 GPa | 1220 ksi | ASTM D790 |
| Izod Impact, Notched | 0.540 J/cm | 1.01 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 23.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
12.8 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 52.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
29.3 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C @Thickness 6.40 mm |
230 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Flammability, UL94 | V-1 @Thickness 2.00 mm |
V-1 @Thickness 0.0787 in |
UL 94 |
Users viewing this material also viewed the following:
- Lehmann & Voss LUVOCOM® 1850/GF/30/TF/15/BK PBT, with glass fiber and PTFE
- Huntsman Araldite GT 9014 US Bisphenol A Epoxy Solid Resin
- Lord Adhesives HPC-5C Hydrogenated Nitrile Butadiene Rubber Coating
- MRC Polymers NAXALOYâ„¢ 780 GF11 PC+PBT Polyester Blend, 11% Glass Fiber Filled
- Techmer ES HiFill® PBT WM35 X
- Teknor Apex Monprene® MP-1627I Thermoplastic Elastomer
- Lubrizol ESTANE® 5715 Ester Based Thermoplastic Polyurethane (European Grade)
- Fainplast Compounds KL 90 Flexible PVC, Insulation for High Temperatures Lead Free
- BASF Formic Acid - 85%
Copyright © lookpolymers.com All Rights Reserved