SABIC Innovative Plastics Lexan® MHL1110 PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Lexan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Lexan® MHL1110 PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Water Absorption | 0.15 % @Time 86400 sec |
0.15 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 123 | 123 | ASTM D785 |
| Tensile Strength, Yield | 61.0 MPa | 8850 psi | SABIC - Japan Method |
| Elongation at Break | 220 % | 220 % | SABIC - Japan Method |
| Flexural Strength | 93.0 MPa | 13500 psi | ASTM D790 |
| Flexural Modulus | 2.20 GPa | 319 ksi | ASTM D790 |
| Izod Impact, Notched | 7.35 J/cm | 13.8 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 70.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
38.9 µin/in-°F @Temperature -22.0 - 86.0 °F |
TMA |
| Deflection Temperature at 0.46 MPa (66 psi) | 130 °C @Thickness 3.20 mm |
266 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | ASTM D257 |
| Dielectric Constant | 3.2 @Frequency 50.0 - 60.0 Hz |
3.2 @Frequency 50.0 - 60.0 Hz |
ASTM D150 |
Users viewing this material also viewed the following:
- Plastcom SLOVASTER® B GF 10 Polybutylene Terephthalate, 10% Glass Fiber
- Pau Tai Unistab LCZ-344K Mixed Metal Liquid Stabilizer Calcium/Zinc for Suspension/Plastisols
- IDI Composites A-205 Thermoset Polyester, Sheet
- LG Chemical LUMID HI1102A(W) PA6, High Impact
- A. Schulman SCHULADUR® B GF30 30% Glass Fiber Reinforced PET
- ExxonMobil Thermrex Series V-32
- Braskem FPT350WV3 Homopolymer Polypropylene
- 3M Scotch® 825 Pouch Tape
- Universal Wire Works 132 Nickel Alloy Welding Wire
- Teknor Apex Sinpolene CPP2030 Polypropylene
Copyright © lookpolymers.com All Rights Reserved