SABIC Innovative Plastics LNP Verton UX06451 PPA
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP VERTON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Verton UX06451 PPA.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Verton* UX06451 is a compound based on Polyphthalamide resin containing Long Glass Fiber.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.63 g/cc | 0.0589 lb/in³ | ASTM D 792 |
| 1.63 g/cc | 0.0589 lb/in³ | ISO 1183 | |
| Moisture Absorption at Equilibrium | 0.30 % @Time 86400 sec |
0.30 % @Time 24.0 hour |
50% RH; ASTM D 570 |
| Linear Mold Shrinkage, Flow | 0.00060 cm/cm @Time 86400 sec |
0.00060 in/in @Time 24.0 hour |
ISO 294 |
| Linear Mold Shrinkage, Transverse | 0.0020 cm/cm @Time 86400 sec |
0.0020 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 274 MPa | 39700 psi | ASTM D 638 |
| 275 MPa | 39900 psi | ISO 527 | |
| Elongation at Break | 1.7 % | 1.7 % | ISO 527 |
| 1.9 % | 1.9 % | ASTM D 638 | |
| Tensile Modulus | 19.0 GPa | 2760 ksi | 1 mm/min; ISO 527 |
| 19.3 GPa | 2800 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 375 MPa | 54400 psi | ISO 178 |
| Flexural Modulus | 17.4 GPa | 2520 ksi | ISO 178 |
| Izod Impact, Notched | 4.11 J/cm @Temperature 23.0 °C |
7.70 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 14.95 J/cm @Temperature 23.0 °C |
28.01 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 40.0 kJ/m² @Temperature 23.0 °C |
19.0 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 75.0 kJ/m² @Temperature 23.0 °C |
35.7 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 14.0 J | 10.3 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 22.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
12.2 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 32.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
17.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
Users viewing this material also viewed the following:
- Polimeri Europa Eraclene® MP 94 High Density Polyethylene - Injection Molding
- LG Chemical LGflex GL100 Plasticizer
- Loxim 330 12HSL Nylon 6
- LyondellBasell Adsylâ„¢ 5C30F Thermoplastic Olefin Resin
- Star Plastics PCGF30 Molding Grade PC with 30% Glass
- Teknor Apex Monprene® MP-1644L3 Thermoplastic Elastomer
- Lubrizol ESTANE® 58564 Ether Based Thermoplastic Polyurethane (European Grade)
- EMS-Grivory Grivory® LV-65H SST black 9288 PA12-GF65
- Abatron AboCast 8103-21 High-Performance Dielectric Epoxy
- A. Schulman POLYFORT™ FPP 3459 Glass Filled Impact Copolymer
Copyright © lookpolymers.com All Rights Reserved