SABIC Innovative Plastics Valox® V9561 PET
| Category | Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Valox® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Valox® V9561 PET.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Flame retardant PET, 30% Glass fiber filled. Offering a good balance in CTI , GWIT , High Heat and mechanical performances.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.71 g/cc | 0.0618 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.250 % | 0.250 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.050 % | 0.050 % | ISO 62 |
| Melt Index of Compound | 33 g/10 min @Load 5.00 kg, Temperature 280 °C |
33 g/10 min @Load 11.0 lb, Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 125 MPa | 18100 psi | 5 mm/min; ISO 527 |
| Tensile Strength, Yield | 125 MPa | 18100 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 2.0 % | 2.0 % | 5 mm/min; ISO 527 |
| Elongation at Yield | 2.0 % | 2.0 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 12.0 GPa | 1740 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 190 MPa | 27600 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 10.75 GPa | 1559 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| 7.00 kJ/m² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 19.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
10.6 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 67.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
37.2 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Vicat Softening Point | 225 °C | 437 °F | Rate B/50; ISO 306 |
| 230 °C | 446 °F | Rate B/120; ISO 306 | |
| Flammability, UL94 | V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
UL 94 by SABIC-IP |
Users viewing this material also viewed the following:
- Polykemi AB SCANAMID 66 A12^ QF2515 Nylon 66,Mineral and Glass Fiber Reinforced
- Iran Petrochemical (PCC) MF3713 High Density Polyethylene
- Solvay Specialty Polymers FOMBLIN® LC200 PFPE Lubricant
- A. Schulman POLYFLAM™ FPP 1007 Talc Filled Homopolymer Polypropylene
- ChevronTexaco A-50 Jet Fuel
- EMS-Grivory Grivory® BG-30 FR PA6-GF30 FR
- Chicago Extruded Metals BioBrass® UNS C62500 Aluminum Bronze
- Chi Mei Wonderloy® PC-540 PC/ABS Alloy - Flame Retardant
Copyright © lookpolymers.com All Rights Reserved