SABIC Innovative Plastics LNP VERTON RX10409D PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP VERTON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP VERTON RX10409D PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* VERTON* RX10409D is a compound based on Nylon 66 containing proprietary fillers. Added feature of this grade is: Structural.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.42 g/cc | 1.42 g/cc | ASTM D792 |
| Density | 1.42 g/cc | 0.0513 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.660 % | 0.660 % | 50% RH, 24 hrs; ASTM D570 |
| 1.00 % | 1.00 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm @Time 86400 sec |
0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm @Time 86400 sec |
0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 199 MPa | 28900 psi | 5 mm/min; ISO 527 |
| 203 MPa | 29400 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.3 % | 2.3 % | 5 mm/min; ISO 527 |
| 2.4 % | 2.4 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 11.8 GPa | 1710 ksi | 1 mm/min; ISO 527 |
| 12.02 GPa | 1743 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 285 MPa | 41300 psi | ISO 178 |
| 302 MPa | 43800 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Yield Strength | 305 MPa | 44200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 10.34 GPa | 1500 ksi | 2 mm/min; ISO 178 |
| 11.1 GPa | 1610 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 2.65 J/cm | 4.96 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 11.7 J/cm | 21.9 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 24.0 kJ/m² | 11.4 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 76.0 kJ/m² | 36.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Charpy Impact Unnotched | 8.80 J/cm² | 41.9 ft-lb/in² | ISO 179/2C |
| Charpy Impact, Notched | 2.20 J/cm² | 10.5 ft-lb/in² | ISO 179/2C |
| Dart Drop, Total Energy | 22.0 J @Temperature 23.0 °C |
16.2 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 7.00 J | 5.16 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 22.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
12.2 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 64.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
35.6 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 258 °C | 496 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 258 °C @Thickness 3.20 mm |
496 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 253 °C | 487 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 253 °C @Thickness 3.20 mm |
487 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- S&E Specialty Polymers TufTech™ GA-92-129 Clear PVC Compound
- Raschig Group EPOXIDUR® 3581 S ZC EP Epoxy Molding Compound
- PolyOne Edgetek® 5209 Black 30 A 1 Acetal (POM) Copolymer
- Imerys Minsparâ„¢ 200 Feldspar
- Momentive Performance Materials RTV5249 Neutral Cure, One Component RTV Adhesive Sealant
- Wellman Wellamid® GFT13-66 XE-WT1 13% Glass Filled, Toughened Nylon 66
- Total Polystyrene Impact 8260 Improved Environmental Stress Crack Resistance High Impact Polystyrene
- Goodfellow Manganin® Copper Resistance Alloy
- Abatron AboSeal 8104-15 Polysulfide, Thixotropic or Self-Leveling Sealant and Caulk
- Armstrong C-1/E Epoxy Adhesive
Copyright © lookpolymers.com All Rights Reserved