SABIC Innovative Plastics LNP VERTON NV004E PC+ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Glass Fiber Filled , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP VERTON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP VERTON NV004E PC+ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP VERTON* NV004E is a compound based on PC+ABS Blend resin containing 20% Long Glass Fiber. Added features of this material include: Easy Molding, Structural.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ASTM D792 |
| 1.30 g/cc | 0.0470 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.100 % | 0.100 % | 23°C / 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm @Time 86400 sec |
0.0020 - 0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0020 - 0.0040 cm/cm @Time 86400 sec |
0.0020 - 0.0040 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0020 - 0.0040 cm/cm @Time 86400 sec |
0.0020 - 0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0020 - 0.0040 cm/cm @Time 86400 sec |
0.0020 - 0.0040 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 119 MPa | 17300 psi | ASTM D638 |
| 124 MPa | 18000 psi | ISO 527 | |
| Elongation at Break | 2.1 % | 2.1 % | ISO 527 |
| 2.4 % | 2.4 % | ASTM D638 | |
| Tensile Modulus | 6.61 GPa | 959 ksi | 50 mm/min; ASTM D638 |
| 7.79 GPa | 1130 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 139 MPa | 20200 psi | ISO 178 |
| 159 MPa | 23100 psi | ASTM D790 | |
| Flexural Modulus | 5.67 GPa | 822 ksi | ASTM D790 |
| 6.97 GPa | 1010 ksi | ISO 178 | |
| Izod Impact, Notched | 1.61 J/cm | 3.02 ft-lb/in | ASTM D256 |
| 1.66 J/cm @Temperature -40.0 °C |
3.11 ft-lb/in @Temperature -40.0 °F |
ASTM D256 | |
| Izod Impact, Unnotched | 5.71 J/cm | 10.7 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 18.0 kJ/m² | 8.57 ft-lb/in² | 80*10*4; ISO 180/1A |
| 17.0 kJ/m² @Temperature -40.0 °C |
8.09 ft-lb/in² @Temperature -40.0 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 41.0 kJ/m² | 19.5 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 16.0 J | 11.8 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 43.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
24.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 44.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
24.7 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 46.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
26.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 47.7 µm/m-°C @Temperature -40.0 - 40.0 °C |
26.5 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 133 °C @Thickness 3.20 mm |
271 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Polymax® Maxelast® F02-081A-6C TPE, Halogen Free Extrusion Grade
- Samsung Cheil Industries Starex® TF-0930 MABS, Unreinforced Scratch Resistant
- Styron XZ 97224.00 Carboxylated SB
- Tisan TISLAMID® 66 20% Glass Fiber Reinforced Nylon 66
- Plenco 4002 Phenolic, Granular, Injection Molded
- Elgiloy® Co-Cr-Ni Alloy, Strip, 20% Cold Reduction, Heat Treated
- ExxonMobil HDPE HD 6605.70 High Density Polyethylene Copolymer Resin
- Solvay Specialty Polymers Solef® 1010 PVDF Homopolymer (discontinued **)
Copyright © lookpolymers.com All Rights Reserved