SABIC Innovative Plastics LNP Thermocomp RW008XXZ PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp RW008XXZ PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* RW008XXZ is a compound based on Nylon 6/6 resin containing Wollastonite.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.52 g/cc | 0.0549 lb/in³ | ISO 1183 |
| 1.53 g/cc | 0.0553 lb/in³ | ASTM D 792 | |
| Moisture Absorption at Equilibrium | 0.86 % | 0.86 % | 23°C / 50% RH; ISO 62 |
| 0.61 % @Time 86400 sec |
0.61 % @Time 24.0 hour |
50% RH; ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D 955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 77.0 MPa | 11200 psi | Type I, 5 mm/min; ASTM D 638 |
| 77.0 MPa | 11200 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 1.6 % | 1.6 % | Type I, 5 mm/min; ASTM D 638 |
| 1.9 % | 1.9 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 6.00 GPa | 870 ksi | 1 mm/min; ISO 527 |
| 6.81 GPa | 988 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 122 MPa | 17700 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 123 MPa | 17800 psi | ISO 178 | |
| Flexural Modulus | 5.51 GPa | 799 ksi | 2 mm/min; ISO 178 |
| 5.88 GPa | 853 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Izod Impact, Notched | 0.310 J/cm @Temperature 23.0 °C |
0.581 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 4.00 J/cm @Temperature 23.0 °C |
7.49 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 2.00 kJ/m² @Temperature 23.0 °C |
0.952 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 24.0 kJ/m² @Temperature 23.0 °C |
11.4 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| 6.00 J @Temperature 23.0 °C |
4.43 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 56.3 µm/m-°C @Temperature -30.0 - 30.0 °C |
31.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| CTE, linear, Transverse to Flow | 70.9 µm/m-°C @Temperature -30.0 - 30.0 °C |
39.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 229 °C | 444 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 242 °C @Thickness 3.20 mm |
468 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 143 °C @Thickness 3.20 mm |
289 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- Rogers Corporation Poron® 4790-79SP-15012 Urethane Shock Pad Foam
- NOVA Chemicals Dytherm® 140R Expandable Polystyrene
- ExxonMobil LL 6202 Injection Molding Resin (discontinued **)
- Lehmann & Voss LUVOCOM® 1105-7568/GY PEEK, with PTFE
- Mallard Creek Polymers ROVENE® 4423 SBR Latex
- KKPC KOSYN KSL 101 Styrene-Butadiene Latex
- SK Chemicals SKYTHANE® US210 Magnetic Binder
- Chase Plastics CP Pryme® PC100HFR Polycarbonate Molding Resin, High Flow, Mold Release
Copyright © lookpolymers.com All Rights Reserved