SABIC Innovative Plastics LNP Thermocomp RF0059 PA 66 (Asia Pacific)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp RF0059 PA 66 (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP STARFLAM* RF0059 is a compound based on Nylon 66 resin containing Flame Retardant, Glass Fiber. Added features of this material include: Flame Retardant.This data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.49 g/cc | 0.0538 lb/in³ | ASTM D 792 |
| Moisture Absorption at Equilibrium | 0.80 % @Time 86400 sec |
0.80 % @Time 24.0 hour |
50% RH; ASTM D 570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 124 MPa | 18000 psi | ASTM D 638 |
| Elongation at Break | 1.6 % | 1.6 % | ASTM D 638 |
| Tensile Modulus | 11.0 GPa | 1600 ksi | 50 mm/min; ASTM D 638 |
| Flexural Strength | 193 MPa | 28000 psi | ASTM D 790 |
| Flexural Modulus | 10.27 GPa | 1490 ksi | ASTM D 790 |
| Izod Impact, Notched | 0.480 J/cm @Temperature 23.0 °C |
0.899 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 2.34 J/cm @Temperature 23.0 °C |
4.38 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Impact Test | 5.00 J @Temperature 23.0 °C |
3.69 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 29.7 µm/m-°C @Temperature -40.0 - 40.0 °C |
16.5 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C @Thickness 3.20 mm |
500 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C @Thickness 3.20 mm |
475 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Flammability, UL94 | V-0 @Thickness 1.70 mm |
V-0 @Thickness 0.0669 in |
UL 94 by SABIC-IP |
Users viewing this material also viewed the following:
- Nylene® 7250 C HS , 50% Glass Fiber/Ceramic Reinforced, Low Warp, High Stiffness Specialty Nylon
- Network Polymers NPP 11-3225
- SABIC Innovative Plastics GELOY XP4034 ASA+PC (Asia Pacific)
- Phillips 66 COPYLENE® CR027 Polypropylene, Homopolymer, Mini-random, BOPP
- DSM Akulon® F232-DH Nylon 6 (European Grade) (Cond) (discontinued **)
- LATI Latamid 6 H2 G/20-V0 PA 6, 20% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant
- 3M FV1225 Removable Vinyl Label Products
Copyright © lookpolymers.com All Rights Reserved