SABIC Innovative Plastics LNP Thermocomp PH0390A PA 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp PH0390A PA 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* PH0390A is a compound based on Nylon 6 resin. Added features of this material include: High Specific Gravity.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 3.80 g/cc | 0.137 lb/in³ | ISO 1183 |
| 3.812 g/cc | 0.1377 lb/in³ | ASTM D 792 | |
| Moisture Absorption at Equilibrium | 0.43 % | 0.43 % | 23°C / 50% RH; ISO 62 |
| 0.18 % @Time 86400 sec |
0.18 % @Time 24.0 hour |
50% RH; ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.0109 cm/cm @Time 86400 sec |
0.0109 in/in @Time 24.0 hour |
ISO 294 |
| 0.011 cm/cm @Time 86400 sec |
0.011 in/in @Time 24.0 hour |
ASTM D 955 | |
| Linear Mold Shrinkage, Transverse | 0.0107 cm/cm @Time 86400 sec |
0.0107 in/in @Time 24.0 hour |
ISO 294 |
| 0.011 cm/cm @Time 86400 sec |
0.011 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 53.0 MPa | 7690 psi | ISO 527 |
| 56.0 MPa | 8120 psi | ASTM D 638 | |
| Elongation at Break | 2.6 % | 2.6 % | ASTM D 638 |
| 2.9 % | 2.9 % | ISO 527 | |
| Tensile Modulus | 6.87 GPa | 996 ksi | 1 mm/min; ISO 527 |
| 7.19 GPa | 1040 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 100 MPa | 14500 psi | ASTM D 790 |
| 101 MPa | 14600 psi | ISO 178 | |
| Flexural Modulus | 5.87 GPa | 851 ksi | ASTM D 790 |
| 6.34 GPa | 920 ksi | ISO 178 | |
| Izod Impact, Notched | 0.320 J/cm @Temperature 23.0 °C |
0.599 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 3.41 J/cm @Temperature 23.0 °C |
6.39 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 26.0 kJ/m² @Temperature 23.0 °C |
12.4 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| 7.00 J @Temperature 23.0 °C |
5.16 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 53.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
29.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 53.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
29.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 54.1 µm/m-°C @Temperature -40.0 - 40.0 °C |
30.1 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 54.1 µm/m-°C @Temperature -40.0 - 40.0 °C |
30.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 197 °C @Thickness 3.20 mm |
387 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 123 °C @Thickness 3.20 mm |
253 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- Ineos G50-100 HDPE
- Samsung Cheil Industries Starex® TX-0510 TRABS, Unreinforced
- Styron Pulse® A35-105 PC/ABS
- Shinkong Synthetic Fibers Shinite® P301T20 PP, 20% Talc Filled
- Wellman Wellamid® 22LHI4 XE-GY1 Nylon 66, Impact Modified
- Dow DOWLEX™ 2083G Linear Low Density Polyethylene
- Eurotec® Tecomid® NB40 KK40 NL PA6, 40% glass fiber/mineral reinforced, natural
- LTL Color Compounds ColorFast® FRPA100X Polycarbonate-ABS Alloy
Copyright © lookpolymers.com All Rights Reserved