SABIC Innovative Plastics LNP Thermocomp OF008E PPS
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp OF008E PPS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* OF008E is a compound based on Polyphenylene Sulfide resin containing Glass Fiber. Added features of this material include: Easy Molding.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.68 g/cc | 0.0607 lb/in³ | ASTM D 792 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm @Time 86400 sec |
0.0020 in/in @Time 24.0 hour |
ASTM D 955 |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm @Time 86400 sec |
0.0080 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 160 MPa | 23200 psi | ISO 527 |
| 178 MPa | 25800 psi | ASTM D 638 | |
| Elongation at Break | 1.2 % | 1.2 % | ISO 527 |
| 1.7 % | 1.7 % | ASTM D 638 | |
| Flexural Strength | 190 MPa | 27600 psi | ISO 178 |
| 248 MPa | 36000 psi | ASTM D 790 | |
| Flexural Modulus | 13.4 GPa | 1940 ksi | ISO 178 |
| 14.26 GPa | 2068 ksi | ASTM D 790 | |
| Izod Impact, Notched | 1.01 J/cm @Temperature 23.0 °C |
1.89 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 5.87 J/cm @Temperature 23.0 °C |
11.0 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² @Temperature 23.0 °C |
2.86 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 21.0 kJ/m² @Temperature 23.0 °C |
9.99 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Coefficient of Friction, Dynamic | 0.66 | 0.66 | ASTM D 3702 Modified |
| Coefficient of Friction, Static | 0.87 | 0.87 | ASTM D 3702 Modified |
| K (wear) Factor | 483 x 10-8 mm³/N-M | 240 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D 3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 26.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
14.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 272 °C | 522 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 261 °C @Thickness 3.20 mm |
502 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- PolyOne Geon™ 81510 Polyvinyl Chloride, Rigid (PVC, Rigid)
- SABIC Innovative Plastics LNP LUBRILOY UA200A PPA (Asia Pacific)
- SABIC Innovative Plastics ULTEM AUT210 PEI (Europe-Africa-Middle East)
- Thermoseal KLINGERSIL® C-4201 General Application Gasketing
- Williams Advanced Alloys Wambraze™ WB975 Solder
- Trelleborg Emerson & Cuming Stycast® XT-1122 Two-Component Epoxy Flexible Encapsulant
- DuPont Performance Polymers Zytel® RS LC3060 NC010 Nylon 610 (Unverified Data**)
- DuPont Teijin Films Mylar® A Polyester Film, 142 Gauge
- Addiplast Addinyl B2H G15 Flame Retardant Nylon 6, 15% Glass Bead
Copyright © lookpolymers.com All Rights Reserved