Polyram Polytron P40N03 Polypropylene, 40% Long Glass Fibers

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 40% Glass Fiber Filler
Manufacturer Polyram
Trade Name Polytron
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polyram Polytron P40N03 Polypropylene, 40% Long Glass Fibers.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Is a chemically coupled 40% long glass fibers reinforced natural polypropylene, heat stabilized, for injection molding applications. These products have significantly improved impact performance characteristics compared to other grades of Polypropylene long fiber thermoplastics. The room temperature Charpy impact properties are 25 to 30% higher at room temperature and at low temperature (-40°C).Information provided by Polyram.
Physical Properties Metric English Comments
Density 1.22 g/cc
0.0441 lb/in³
ISO 1183
Linear Mold Shrinkage 0.0010 - 0.0020 cm/cm
0.0010 - 0.0020 in/in
ISO 2577
Mechanical Properties Metric English Comments
Tensile Strength, Yield 115 MPa
16700 psi
ISO 527
Elongation at Break 2.8 %
2.8 %
ISO 527
Tensile Modulus 7.80 GPa
1130 ksi
ISO 527
Flexural Strength 180 MPa
26100 psi
ISO 178
Flexural Modulus 8.00 GPa
1160 ksi
ISO 178
Izod Impact, Notched (ISO) 21.0 kJ/m²

@Temperature 22.0 °C
9.99 ft-lb/in²

@Temperature 71.6 °F
ISO 180
23.0 kJ/m²

@Temperature -30.0 °C
10.9 ft-lb/in²

@Temperature -22.0 °F
ISO 180
Charpy Impact Unnotched 7.50 J/cm²

@Temperature 23.0 °C
35.7 ft-lb/in²

@Temperature 73.4 °F
ISO 179
8.00 J/cm²

@Temperature -30.0 °C
38.1 ft-lb/in²

@Temperature -22.0 °F
ISO 179
Charpy Impact, Notched 2.30 J/cm²

@Temperature 23.0 °C
10.9 ft-lb/in²

@Temperature 73.4 °F
ISO 179
2.40 J/cm²

@Temperature -30.0 °C
11.4 ft-lb/in²

@Temperature -22.0 °F
ISO 179
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 151 °C
304 °F
ISO 75