SABIC Innovative Plastics LNP Thermocomp OC008A PPS - Branched
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp OC008A PPS - Branched.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* OC008A is a compound based on Branched Polyphenylene Sulfide containing Carbon Fiber.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.49 g/cc | 1.49 g/cc | ASTM D 792 |
| Density | 1.49 g/cc | 0.0538 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.040 % | 0.040 % | 23°C / 50% RH; ISO 62 |
| 0.040 % @Time 86400 sec |
0.040 % @Time 24.0 hour |
50% RH; ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0060 cm/cm @Time 86400 sec |
0.0030 - 0.0060 in/in @Time 24.0 hour |
ASTM D 955 |
| Linear Mold Shrinkage, Transverse | 0.0020 - 0.0050 cm/cm @Time 86400 sec |
0.0020 - 0.0050 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 162 MPa | 23500 psi | 5 mm/min; ISO 527 |
| 192 MPa | 27800 psi | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Break | 5.1 % | 5.1 % | 5 mm/min; ISO 527 |
| 5.3 % | 5.3 % | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Modulus | 74.84 GPa | 10850 ksi | 50 mm/min; ASTM D 638 |
| Flexural Strength | 259 MPa | 37600 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 264 MPa | 38300 psi | ISO 178 | |
| Flexural Modulus | 28.3 GPa | 4100 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 28.97 GPa | 4202 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.530 J/cm @Temperature 23.0 °C |
0.993 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 5.24 J/cm @Temperature 23.0 °C |
9.82 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² @Temperature 23.0 °C |
1.90 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 22.0 kJ/m² @Temperature 23.0 °C |
10.5 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 11.6 µm/m-°C @Temperature -30.0 - 30.0 °C |
6.44 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| CTE, linear, Transverse to Flow | 22.6 µm/m-°C @Temperature -30.0 - 30.0 °C |
12.6 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 278 °C | 532 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 268 °C @Thickness 3.20 mm |
514 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 276 °C | 529 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 246 °C @Thickness 3.20 mm |
475 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- Nye Lubricants 438 (SO) Synthetic Oil
- PolyOne Maxxam™ PP CS 75 Polypropylene, Unspecified (PP, Unspecified)
- PolyOne Geon™ Vinyl Flexible B7D01 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Multibase Multi-Flex® A 7802 TPE Blk Thermoplastic Elastomer
- SABIC Innovative Plastics LNP LUBRICOMP RX03643H PA 66 (Asia Pacific)
- Sharadaa Ceramics ZAP 008 Smart Cast Application
- ELASTO UK Dryflex® 602850S SEBS Based Material, Filled Qualities, 85A Hardness, Black
- Chi Mei Polylac® PA-764 ABS - Flame Retardant
- AK Steel ZINCGRIP® Hot Dip Galvanized Carbon Steel, Extra Deep Drawing Steel (EDDS), Standard Grade
- BASF Ultramid® B3EG3 BK00564 15% Glass Filled PA6 (Dry)
Copyright © lookpolymers.com All Rights Reserved