SABIC Innovative Plastics LNP Thermocomp LF004 PEEK
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp LF004 PEEK.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* LF004 is a compound based on Polyetheretherketone resin containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.46 g/cc | 1.46 g/cc | ASTM D 792 |
| Density | 1.45 g/cc | 0.0524 lb/in³ | ASTM D 792 |
| 1.46 g/cc | 0.0527 lb/in³ | ISO 1183 | |
| Moisture Absorption at Equilibrium | 0.19 % @Time 86400 sec |
0.19 % @Time 24.0 hour |
50% RH; ASTM D 570 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0060 cm/cm @Time 86400 sec |
0.0030 - 0.0060 in/in @Time 24.0 hour |
ASTM D 955 |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.010 cm/cm @Time 86400 sec |
0.0070 - 0.010 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 151 MPa | 21900 psi | Type I, 5 mm/min; ASTM D 638 |
| 152 MPa | 22000 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 5.0 % | 5.0 % | 5 mm/min; ISO 527 |
| 5.4 % | 5.4 % | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Modulus | 14.19 GPa | 2058 ksi | 50 mm/min; ASTM D 638 |
| Flexural Strength | 223 MPa | 32300 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 8.31 GPa | 1210 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 9.64 GPa | 1400 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.850 J/cm @Temperature 23.0 °C |
1.59 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 8.72 J/cm @Temperature 23.0 °C |
16.3 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² @Temperature 23.0 °C |
3.33 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 54.0 kJ/m² @Temperature 23.0 °C |
25.7 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 242 °C | 468 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 280 °C @Thickness 3.20 mm |
536 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 278 °C @Thickness 3.20 mm |
532 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- M Chemical GUARD DOGâ„¢ UV5411 Benzotriazole UV Absorber, Powder and LD Pellet
- MarkeTech AO 98 Aluminum Oxide Ceramic Substrate, 98% Purity
- Lotte Chemical Titan TITANPRO® PM383 Polypropylene homopolymer
- American Elements Copper Nanoparticles
- Ascend Performance Materials Vydyne® R525H BK02 Nylon 66, 25% Glass Reinforced, Conditioned
- Bisalloy Steels BisPlate 400 Thickness >80-100 mm
- Pau Tai Unistab BC-468A Mixed Metal Liquid Stabilizer for PVC Cadmium/Barium/Zinc Self-Lubricating
- SABIC Innovative Plastics LNP VERTON RV00CEXP PA 66 (Europe-Africa-Middle East)
- Huntsman PE2053 Injection Molding Polyethylene (discontinued **)
Copyright © lookpolymers.com All Rights Reserved