SABIC Innovative Plastics LNP Thermocomp HF00ASU PA11 (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Nylon , Nylon 11 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp HF00ASU PA11 (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* HF00ASU is a compound based on PA11 resin containing Glass Fiber. Added features include; Heat Stabilized, UV-Stabilized.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in³ | ISO 1183 |
| Water Absorption | 0.14 % @Temperature 23.0 °C, Time 86400 sec |
0.14 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm | 0.0020 in/in | SABIC Method |
| 0.0040 cm/cm @Time 86400 sec |
0.0040 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.012 cm/cm @Time 86400 sec |
0.012 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 158 MPa | 22900 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 5.6 % | 5.6 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 9.80 GPa | 1420 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 223 MPa | 32300 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 10.3 GPa | 1490 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 27.0 kJ/m² @Temperature 23.0 °C |
12.8 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 87.0 kJ/m² @Temperature 23.0 °C |
41.4 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 16.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
8.89 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 114 µm/m-°C @Temperature 23.0 - 60.0 °C |
63.3 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 179 °C | 354 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
Users viewing this material also viewed the following:
- Ovation Polymers Nemcon™ H PC DP105/X3 BK Polycarbonate
- SABIC Innovative Plastics LNP LUBRICOMP DL0029E PC (Europe-Africa-Middle East)
- Hybrid Plastics POSS® MA0742 MethacryltrimethylsiloxyIsobutyl-POSS®
- SABIC Innovative Plastics LNP LUBRICOMP ML004S PP (Asia Pacific)
- SIDPEC EGYPTENE® HD 5403 EA HDPE Blow Molding
- Unifrax Fiberfrax® HS70C High Purity High-Index Fiber
- Trelleborg Commercial Neoprene® C653 Chloroprene
- DSM Akulon® K224-HG6U (Dry) 33% Glass Reinforced Nylon 6 (North America)
- 3M 4412G Extreme Sealing Tape
- API Megol AM DP1741 SEBS Adhesion Modified Overmolding for PA
Copyright © lookpolymers.com All Rights Reserved