SABIC Innovative Plastics LNP THERMOTUF WF006I PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Thermotuf |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOTUF WF006I PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOTUF* WF006I is a compound based on PBT containing 30% Glass Fiber. Added features of this material include: High Impact.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.47 g/cc | 0.0531 lb/in³ | ISO 1183 |
| 1.474 g/cc | 0.05325 lb/in³ | ASTM D792 | |
| Linear Mold Shrinkage, Flow | 0.0029 cm/cm @Time 86400 sec |
0.0029 in/in @Time 24.0 hour |
ISO 294 |
| 0.0030 cm/cm @Time 86400 sec |
0.0030 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0129 cm/cm @Time 86400 sec |
0.0129 in/in @Time 24.0 hour |
ISO 294 |
| 0.013 cm/cm @Time 86400 sec |
0.013 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 106 MPa | 15400 psi | ASTM D638 |
| Tensile Strength, Yield | 107 MPa | 15500 psi | ASTM D638 |
| 109 MPa | 15800 psi | ISO 527 | |
| Elongation at Break | 2.8 % | 2.8 % | ISO 527 |
| 3.9 % | 3.9 % | ASTM D638 | |
| Elongation at Yield | 2.1 % | 2.1 % | ISO 527 |
| 3.2 % | 3.2 % | ASTM D638 | |
| Tensile Modulus | 6.52 GPa | 946 ksi | 1 mm/min; ISO 527 |
| 8.96 GPa | 1300 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 173 MPa | 25100 psi | ASTM D790 |
| 181 MPa | 26300 psi | ISO 178 | |
| Flexural Modulus | 7.51 GPa | 1090 ksi | ASTM D790 |
| 8.62 GPa | 1250 ksi | ISO 178 | |
| Izod Impact, Notched | 1.86 J/cm | 3.48 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 9.98 J/cm | 18.7 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 20.0 kJ/m² | 9.52 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 64.0 kJ/m² | 30.5 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 17.0 J | 12.5 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C @Thickness 3.20 mm |
410 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- MV Labs CO730 Na3Co(NO2)6 Sodium hexanitrocobaltate(III)
- MV Labs NI100 Ni(C2H3O2)2·4H2O Nickel acetate tetrahydrate
- Omnia Plastica PA6 GF Akulon GF - Dry
- Materion Beryllium Copper Alloy 3 Rod and Bar; H (TD04) Temper; up to 76 mm (UNS C17510)
- Momentive Performance Materials RTV41 White General Purpose Potting/Encapsulating Compound
- Daikin NEOFLON NF-0025 FEP Film
- AK Steel CL 2/ SAE J1392 045 XLK, Grade 50 Cold Rolled Carbon Steel, High Strength Low Alloy Steel (HSLAS)
- Austin Novel Materials Texalan® 282A Polyester-based TPU
- NOVA Chemicals Sclair® 2607-UV9 HDPE Injection Molding Resin (discontinued **)
Copyright © lookpolymers.com All Rights Reserved