SABIC Innovative Plastics LNP THERMOTUF VX99809 Super Tough Nylon
| Category | Polymer , Thermoplastic , Nylon |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Thermotuf |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOTUF VX99809 Super Tough Nylon.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Super Tough Nylon, Proprietary Filler(s),
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.08 g/cc | 0.0390 lb/in³ | ISO 1183 |
| 1.084 g/cc | 0.03916 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.920 % | 0.920 % | 50% RH, 24 hrs; ASTM D570 |
| 1.90 % | 1.90 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec |
>= 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.020 - 0.040 cm/cm @Time 86400 sec |
0.020 - 0.040 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 40.0 MPa | 5800 psi | Type I, 5 mm/min; ASTM D638 |
| 41.0 MPa | 5950 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 42.0 MPa | 6090 psi | 5 mm/min; ISO 527 |
| 43.0 MPa | 6240 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 75.4 % | 75.4 % | Type I, 5 mm/min; ASTM D638 |
| 129 % | 129 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 3.6 % | 3.6 % | 5 mm/min; ISO 527 |
| 3.9 % | 3.9 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 1.88 GPa | 273 ksi | 1 mm/min; ISO 527 |
| 1.98 GPa | 287 ksi | 50 mm/min; ASTM D638 | |
| Flexural Modulus | 1.22 GPa | 177 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 1.30 GPa | 189 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 8.85 J/cm | 16.6 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 13.3 J/cm | 24.9 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 82.0 kJ/m² | 39.0 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 145 kJ/m² | 69.0 ft-lb/in² | 80*10*4; ISO 180/1U |
| Impact Test | 49.0 J | 36.1 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 178 °C @Thickness 3.20 mm |
352 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- MV Labs PT465 K2PtCl6 Potassium hexachloroplatinate(IV)
- LyondellBasell Aquathene® CM04482 Catalyst Masterbatch
- SABIC Innovative Plastics LNP LUBRICOMP WI001 PBT (Europe-Africa-Middle East)
- Solvay Specialty Polymers Tecnoflon® P 457 Fluoroelastomer
- Shandong Rike Chemical HELIâ„¢ HL-275D PVC Processing Aid Series (PA)
- Saint-Gobain Chemlam® 4 Value Industrial Laminate
- Samsung Cheil Industries Infino® MKD-1015 PA, Glass Filled
- Covestro Apec® 2095 Polycarbonate
Copyright © lookpolymers.com All Rights Reserved