Solvay Specialty Polymers Mindel® S-1000 Modified Polysulfone (discontinued **)
| Category | Polymer , Thermoplastic , Polysulfone (PSU) , Polysulfone, Modified |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Specialty Polymers Mindel® S-1000 Modified Polysulfone
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
This product line was acquired by Solvay Advanced Polymers from BP Amoco in November 2001.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | ASTM D792 |
| Water Absorption | 0.20 % | 0.20 % | in 24 hours per ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 66.0 MPa | 9570 psi | ASTM D638 |
| Elongation at Break | 100 % | 100 % | ASTM D638 |
| Elongation at Yield | 6.0 % | 6.0 % | ASTM D638 |
| Tensile Modulus | 2.41 GPa | 350 ksi | ASTM D638 |
| Flexural Yield Strength | 97.0 MPa | 14100 psi | ASTM D790 |
| Flexural Modulus | 2.63 GPa | 381 ksi | ASTM D790 |
| Izod Impact, Notched | 0.900 J/cm | 1.69 ft-lb/in | ASTM D256 |
| Tensile Impact Strength | 270 kJ/m² | 128 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 103 µm/m-°C @Temperature 20.0 °C |
57.2 µin/in-°F @Temperature 68.0 °F |
ASTM E381 |
| CTE, linear, Transverse to Flow | 103 µm/m-°C @Temperature 20.0 °C |
57.2 µin/in-°F @Temperature 68.0 °F |
ASTM E381 |
| Deflection Temperature at 1.8 MPa (264 psi) | 149 °C | 300 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 3.30 mm |
V-0 @Thickness 0.130 in |
|
| V-0 @Thickness 3.30 mm |
V-0 @Thickness 0.130 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 3.1 @Frequency 1000 Hz |
3.1 @Frequency 1000 Hz |
ASTM D150 |
| Dielectric Strength | 20.0 kV/mm @Thickness 0.320 mm |
508 kV/in @Thickness 0.0126 in |
ASTM D149 |
| Dissipation Factor | 0.0010 @Frequency 1000 Hz |
0.0010 @Frequency 1000 Hz |
ASTM D150 |
Users viewing this material also viewed the following:
- Polimeri Europa Dutral® TER 4039 Ethylene - Propylene - Diene Terpolymer
- Osprey Metals Oxygen-Free Electronic Copper Powder (Grade 80% - 22)
- SABIC Innovative Plastics LNP COLORCOMP EX12304C PEI (Asia Pacific)
- Chevron Phillips MarFlex® 7120 LLDPE Blown & Cast Film Resin (discontinued **)
- Lubriplate APG 80W-140 Petroleum-Based Gear, Bearing, & Recirculating Oil
- Mitsubishi Xantar® F 25 UR Polycarbonate
- Solvay TECHNYLSTARâ„¢ S 218 V35 PA6, 35% glass filled, Conditioned
- Trelleborg R350 Natural Rubber Polyisoprene
- Ascend Performance Materials Vydyne® ECO315 BK13 Nylon 66, Flame Retardant, Conditioned
- Haynes 625 alloy, 40% cold reduction, 1010°C anneal for 5 minutes
Copyright © lookpolymers.com All Rights Reserved