SABIC Innovative Plastics LNP THERMOCOMP ZF004 PPE+PS
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP ZF004 PPE+PS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* ZF004 is a compound based on PPE+PS resin containing 20% Glass Fiber.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | ASTM D792 |
| 1.22 g/cc | 0.0441 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.0900 % | 0.0900 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0900 % | 0.0900 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 79.0 MPa | 11500 psi | 5 mm/min; ISO 527 |
| 80.0 MPa | 11600 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.8 % | 1.8 % | Type I, 5 mm/min; ASTM D638 |
| 1.8 % | 1.8 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 6.50 GPa | 943 ksi | 1 mm/min; ISO 527 |
| 6.57 GPa | 953 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 118 MPa | 17100 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 121 MPa | 17500 psi | ISO 178 | |
| Flexural Modulus | 6.27 GPa | 909 ksi | 2 mm/min; ISO 178 |
| 6.41 GPa | 930 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.690 J/cm | 1.29 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.90 J/cm | 7.31 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 31.0 kJ/m² | 14.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 12.0 J @Temperature 23.0 °C |
8.85 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 68.3 µm/m-°C @Temperature -30.0 - 30.0 °C |
37.9 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 53.6 µm/m-°C @Temperature -30.0 - 30.0 °C |
29.8 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 137 °C | 279 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 138 °C @Thickness 3.20 mm |
280 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 131 °C | 268 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 131 °C @Thickness 3.20 mm |
268 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Rogers Corporation RO4534 Ceramic-Filled, Glass-Reinforced Hydrocarbon Laminate
- LATI LATAMID 12 H FE90 Nylon 12 Base Magnetizable Compound (Unverified Data**)
- Kinetics MIM 12 Chrome
- Sharadaa Ceramics HA 60 High Alumina Brick
- DuPont Elvax® 3134SBZ Ethylene Vinyl Acetate
- Carpenter MP35N* Ni-Co-Cr-Mo Alloy, 15% Cold Reduction + Aged 538°C (1000°F)/4hr/AC
- 3M FM142 Indoor UL Recognized Computer Imprintable Clear Polyester Label Product
- Total Lacqrene® 4801 (discontinued **)
Copyright © lookpolymers.com All Rights Reserved