- SABIC Innovative Plastics LNP THERMOCOMP YF002 POLYESTER ELASTOMER
SABIC Innovative Plastics LNP THERMOCOMP YF002 POLYESTER ELASTOMER
| Category | Polymer , Thermoplastic , Polyester, TP |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP YF002 POLYESTER ELASTOMER.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* YF002 is a compound based on Poyester Elastomer containing 10% Glass Fiber. Added feature of this grade is: High Modulus.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.30 g/cc | 1.30 g/cc | ASTM D792 |
| Density | 1.30 g/cc | 0.0470 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec |
>= 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 58.0 MPa | 8410 psi | Type I, 5 mm/min; ASTM D638 |
| 59.0 MPa | 8560 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | Type I, 5 mm/min; ASTM D638 |
| 60.0 MPa | 8700 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 12 % | 12 % | 5 mm/min; ISO 527 |
| 13 % | 13 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 9.0 % | 9.0 % | Type I, 5 mm/min; ASTM D638 |
| 9.0 % | 9.0 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 2.29 GPa | 332 ksi | 1 mm/min; ISO 527 |
| 2.53 GPa | 367 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 62.0 MPa | 8990 psi | ISO 178 |
| Flexural Modulus | 1.86 GPa | 270 ksi | 2 mm/min; ISO 178 |
| 2.00 GPa | 290 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 1.58 J/cm | 2.96 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 9.85 J/cm | 18.5 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 64.0 kJ/m² | 30.5 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 6.00 J @Temperature 23.0 °C |
4.43 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 9.00 J | 6.64 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 67.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
37.2 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 135 µm/m-°C @Temperature -30.0 - 30.0 °C |
75.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 194 °C | 381 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 205 °C @Thickness 3.20 mm |
401 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 153 °C | 307 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 184 °C @Thickness 3.20 mm |
363 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- MV Labs SC400 ScCl3·xH2O Scandium chloride hydrate
- Owens Corning Glass Fiber Reinforced Polyurethane, Milled Fibers (RRIM), 13 wt.% glass
- SABIC Innovative Plastics Lexan® 925A PC (Asia Pacific)
- Chevron Phillips HiD® 94312 HDPE Extrusion Coating Resin (discontinued **)
- Global HI-650 High Impact Polystyrene
- Flint Hills P6C6B-134 General Purpose Impact Copolymer Polypropylene
- Stellarchem GP-945 TPE Compound
- UCAR Carbon UCAR® ATA Isostatic Molded Graphite
- Crucible Steel 416R Chromium Stainless Steel