SABIC Innovative Plastics LNP THERMOCOMP WH0420A_GY5A749 PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP WH0420A_GY5A749 PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
4.2 specific gravity, PBT, gray
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 4.20 g/cc | 0.152 lb/in³ | ASTM D792 |
| 4.20 g/cc | 0.152 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.0500 % | 0.0500 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0700 % | 0.0700 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.016 - 0.018 cm/cm @Time 86400 sec |
0.016 - 0.018 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.014 - 0.016 cm/cm @Time 86400 sec |
0.014 - 0.016 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 25.0 MPa | 3630 psi | 5 mm/min; ISO 527 |
| 26.0 MPa | 3770 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 27.0 MPa | 3920 psi | Type I, 5 mm/min; ASTM D638 |
| 27.0 MPa | 3920 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 9.7 % | 9.7 % | 5 mm/min; ISO 527 |
| 18.6 % | 18.6 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 8.4 % | 8.4 % | 5 mm/min; ISO 527 |
| 12.2 % | 12.2 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 1.80 GPa | 261 ksi | 1 mm/min; ISO 527 |
| 1.93 GPa | 280 ksi | 50 mm/min; ASTM D638 | |
| Flexural Yield Strength | 46.0 MPa | 6670 psi | 2 mm/min; ISO 178 |
| 50.0 MPa | 7250 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 1.84 GPa | 267 ksi | 2 mm/min; ISO 178 |
| 1.91 GPa | 277 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 1.17 J/cm | 2.19 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 11.8 J/cm | 22.1 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 78.0 kJ/m² | 37.1 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 16.0 J @Temperature 23.0 °C |
11.8 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 92.4 µm/m-°C @Temperature -30.0 - 30.0 °C |
51.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 94.9 µm/m-°C @Temperature -30.0 - 30.0 °C |
52.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM E 831 |
| Deflection Temperature at 1.8 MPa (264 psi) | 53.0 °C | 127 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 51.0 °C @Thickness 3.20 mm |
124 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Polymax® Maxelast® P3955T TPE, PP Overmold or Standalone use
- Resinlab® CYNERGY CA6014 Adhesive
- Honeywell Capran® Emblem™ 1230 Bi-Axially Oriented Nylon Film (discontinued **)
- Honeywell Capran® NyLid™ WMB 250 Nylon Lidding Film (discontinued **)
- LyondellBasell Pro-fax 6331W Polypropylene Homopolymer, Antistat
- LyondellBasell Petrothene® GA502023 Linear Low Density Polyethylene
- Schott N-SF6 Glass
- ExxonMobil Label-Lyte™ 30LL-101 OPP Film
- PolyOne Edgetek® PI-20GF/000 Polyetherimide (PEI), Glass Filled (discontinued **)
- ExxonMobil CM-S Mobilgrease CM Series
Copyright © lookpolymers.com All Rights Reserved