SABIC Innovative Plastics LNP THERMOCOMP WFB44 PBT (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP WFB44 PBT (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* WFB44 is a compound based on Polybutylene Terephalate resin containing Glass Fiber, Glass Bead.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.62 g/cc | 0.0585 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0050 cm/cm | 0.0020 - 0.0050 in/in | on Tensile Bar; SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 100 MPa | 14500 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 2.8 % | 2.8 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 8.00 GPa | 1160 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 140 MPa | 20300 psi | 2 mm/min; ISO 178 |
| Flexural Yield Strength | 157 MPa | 22800 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 7.20 GPa | 1040 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 35.0 kJ/m² | 16.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 39.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
21.7 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 99.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
55.0 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 219 °C | 426 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 192 °C | 378 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | ASTM D257 |
| Comparative Tracking Index | 325 V | 325 V | IEC 60112 |
Users viewing this material also viewed the following:
- Quantum Composites LYTEX® 4197 55% Carbon Fiber Reinforced Epoxy SMC
- Mallard Creek Polymers ROVENE® 6017 Styrene-Acrylic Emulsion
- SABIC Innovative Plastics ULTEM 4000 PEI
- Lubrizol ESTANE® T5213 Ether Based Thermoplastic Polyurethane (European Grade)
- Master Bond MB600G Aqueous Based Electrically Conductive Sodium Silicate Coating
- Total 50100.2 HDPE blow molding, sheet, thermoforming resin
- Trelleborg Neoprene® C627 Chloroprene
- DuPont Teijin Films Mylar® C Polyester Film, 24 Gauge
- Aclo Accutech Polypropylene Copolymer CP0436G30CL Glass Reinforced
- Atom Adhesives AA-BOND 2112 Epoxy Adhesive
Copyright © lookpolymers.com All Rights Reserved