SABIC Innovative Plastics LNP THERMOCOMP UX04509 PPA
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP UX04509 PPA.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* UX04509 is a compound based on Polyphthalamide resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.38 g/cc | 1.38 g/cc | ASTM D792 |
| Density | 1.37 g/cc | 0.0495 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.190 % | 0.190 % | 50% RH, 24 hrs; ASTM D570 |
| 0.290 % | 0.290 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0050 cm/cm @Time 86400 sec |
0.0020 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0080 cm/cm @Time 86400 sec |
0.0050 - 0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 293 MPa | 42500 psi | 5 mm/min; ISO 527 |
| 307 MPa | 44500 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 293 MPa | 42500 psi | 5 mm/min; ISO 527 |
| 307 MPa | 44500 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.1 % | 1.1 % | 5 mm/min; ISO 527 |
| 1.2 % | 1.2 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 1.1 % | 1.1 % | 5 mm/min; ISO 527 |
| 1.2 % | 1.2 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 34.44 GPa | 4995 ksi | 1 mm/min; ISO 527 |
| 36.82 GPa | 5340 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 424 MPa | 61500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 425 MPa | 61600 psi | ISO 178 | |
| Flexural Yield Strength | 424 MPa | 61500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 28.83 GPa | 4181 ksi | 2 mm/min; ISO 178 |
| 29.3 GPa | 4250 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.690 J/cm | 1.29 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 7.23 J/cm | 13.5 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 47.0 kJ/m² | 22.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 6.00 J @Temperature 23.0 °C |
4.43 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 28.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
15.6 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 27.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
15.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 301 °C | 574 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 303 °C @Thickness 3.20 mm |
577 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 283 °C | 541 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 289 °C @Thickness 3.20 mm |
552 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Outokumpu 4311 Cr-Ni Austenitic Stainless Steel
- Niche Polymer PA6GF43N Nylon 6, 43% Glass Fiber Filled
- ExxonMobil Escorene® LL-1117 LLDPE Film/Sandwich Bag Resin (discontinued **)
- Ineos K44-08-123 HDPE Copolymer with Carbon Black
- ITW Plexus Plexusâ„¢ MA821 Methacrylate Adhesive
- Aclo Accutech Polypropylene Homopolymer HP0339W10L Wollastonite Reinforced
- Pau Tai #401, Modifier for PVC
Copyright © lookpolymers.com All Rights Reserved