SABIC Innovative Plastics LNP THERMOCOMP UF009S PPA
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP UF009S PPA.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* UF009S is a compound based on Polyphthalamide resin containing 45% Glass Fiber. Added features of this material include: Heat Stabilized.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.64 g/cc | 0.0592 lb/in³ | ISO 1183 |
| 1.645 g/cc | 0.05943 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.250 % | 0.250 % | 50% RH, 24 hrs; ASTM D570 |
| 0.370 % | 0.370 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0018 cm/cm @Time 86400 sec |
0.0018 in/in @Time 24.0 hour |
ISO 294 |
| 0.0020 cm/cm @Time 86400 sec |
0.0020 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0046 cm/cm @Time 86400 sec |
0.0046 in/in @Time 24.0 hour |
ISO 294 |
| 0.0050 cm/cm @Time 86400 sec |
0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 242 MPa | 35100 psi | ASTM D638 |
| 253 MPa | 36700 psi | ISO 527 | |
| Elongation at Break | 1.7 % | 1.7 % | ASTM D638 |
| 1.8 % | 1.8 % | ISO 527 | |
| Tensile Modulus | 20.35 GPa | 2952 ksi | 50 mm/min; ASTM D638 |
| 22.74 GPa | 3298 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 386 MPa | 56000 psi | ISO 178 |
| 392 MPa | 56900 psi | ASTM D790 | |
| Flexural Modulus | 18.33 GPa | 2659 ksi | ISO 178 |
| 18.76 GPa | 2721 ksi | ASTM D790 | |
| Izod Impact, Notched | 1.70 J/cm | 3.18 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 13.45 J/cm | 25.20 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 14.0 kJ/m² | 6.66 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 82.0 kJ/m² | 39.0 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 15.0 J | 11.1 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 4.00 J | 2.95 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 258 °C @Thickness 3.20 mm |
496 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- RheTech Products T20P100-01 20% Talc Reinforced Polypropylene, Black
- M. Holland Company CP400 Polypropylene Copolymer
- Kennametal Stellite Stoody® 6 Cobalt-Base Cast Alloy
- Michelman® Michem® Emulsion 94340 Nonionic polypropylene emulsion
- Eastman Eastar CN015 Copolyester, High Flow Grade with Mold Release
- Conforma Clad WC 210 Tungsten Carbide-Nickel Cladding
- Arlon UltraPad™ 55073R031 Silicone-Based Press Pad
- 3M Scotchcal™ ElectroCut™ 7725-90 Graphic Film
- Quadrant EPP Quadrant LSG PSU extruded (ISO Data)
Copyright © lookpolymers.com All Rights Reserved