SABIC Innovative Plastics LNP THERMOCOMP RX98372H PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP RX98372H PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* RX98372H is a compound based on Nylon 66 resin containing Proprietary Fillers. Characteristics of this grade are: Healthcare.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.69 g/cc | 1.69 g/cc | ASTM D792 |
| Density | 1.69 g/cc | 0.0611 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.390 % | 0.390 % | 50% RH, 24 hrs; ASTM D570 |
| 0.510 % | 0.510 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm @Time 86400 sec |
0.0040 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.0090 cm/cm @Time 86400 sec |
0.0070 - 0.0090 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 243 MPa | 35200 psi | 5 mm/min; ISO 527 |
| 245 MPa | 35500 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.9 % | 1.9 % | Type I, 5 mm/min; ASTM D638 |
| 1.9 % | 1.9 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 21.35 GPa | 3097 ksi | 1 mm/min; ISO 527 |
| 21.86 GPa | 3171 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 383 MPa | 55500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 383 MPa | 55500 psi | ISO 178 | |
| Flexural Modulus | 19.5 GPa | 2830 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 20.3 GPa | 2940 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 1.82 J/cm | 3.41 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 11.4 J/cm | 21.4 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 64.0 kJ/m² | 30.5 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 9.00 J @Temperature 23.0 °C |
6.64 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 4.00 J | 2.95 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 15.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
8.33 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 36.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
20.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 260 °C @Thickness 3.20 mm |
500 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 253 °C | 487 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 253 °C @Thickness 3.20 mm |
487 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Nye Lubricants 131A (DMO) Delicate Machinery Oil
- Plastcom SLOVAMID 6 GF 15 T 25 LTS PA6, 15% glass fibre, 25% mineral filling
- PolyOne Maxxam™ PPH-40T Nat Polypropylene Homopolymer (PP Homopolymer)
- Quadrant EPP Proteus® PP, Natural Homopolymer Polypropylene (ASTM Product Data Sheet)
- Intercontinental Polymers HoPBN 312 HoPBN Polymer Type - Clear, Polyester Pellets
- Iran Petrochemical (PCC) PET BG-785 Polyethylene Terephthalate
- LyondellBasell Adsylâ„¢ 3 C 39 F HP Polypropylene Copolymer
- Zircar Zirconia ZOG Single Crystal Zirconia Grog Insulation
Copyright © lookpolymers.com All Rights Reserved