SABIC Innovative Plastics LNP THERMOCOMP PX12419 PA 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP PX12419 PA 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* PX12419 is a compound based on Nylon 6 containing Carbon Fiber. Added features of this grade include: Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.26 g/cc | 1.26 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 233 MPa | 33800 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 24.9 GPa | 3610 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 345 MPa | 50000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 19.0 GPa | 2760 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 0.990 J/cm | 1.85 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.22 J/cm | 15.4 ft-lb/in | ASTM D4812 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 100 - 1000 ohm | 100 - 1000 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycolac® DL100 ABS (Europe-Africa-Middle East)
- Multibase 7-9600 Dow-Corning Soft Filling Elastomer Parts A and B
- SSAB Tunnplat Aluzink F36A Metal-coated Mild Steel
- DuPont Conpol™ 10AF Ethylene-Methacrylic Acid Additive Resin
- A. Schulman POLYBATCH™ Popular Choice White HS80660 Concentrate Based In Polystyrene
- DuPont Teijin Films Mylar® E Polyester Film, 200 Gauge
- E-Polymers TEKANATE™ G730FR , Flame Retardant, 30% Glass Fiber Reinforced Poly Carbonate
- Arlon R34572R005 0.005" (0.127 mm) Cured Silicone Rubber with Fiberglass Substrate
- 3A Composites Core Materials AIREX® C71.75 Elevated Temperature Structural Foam
- Arkema Group Orgalloy® LT 6040 Flexible Nylon Alloy (Conditioned)
Copyright © lookpolymers.com All Rights Reserved