SABIC Innovative Plastics LNP THERMOCOMP NX07354P PC+ABS (Asia Pacific)
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP NX07354P PC+ABS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
This is a PC/ABS compound with improved plating performance, a good candidate for Laser Direct Structuring applications.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | ASTM D792 |
| 1.22 g/cc | 0.0441 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.0500 % | 0.0500 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0069 cm/cm | 0.0069 in/in | SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0061 cm/cm | 0.0061 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 40.0 MPa | 5800 psi | 5 mm/min; ISO 527 |
| 42.0 MPa | 6090 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 41.0 MPa | 5950 psi | 5 mm/min; ISO 527 |
| 42.0 MPa | 6090 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 72.7 % | 72.7 % | Type I, 5 mm/min; ASTM D638 |
| 74.2 % | 74.2 % | Flexural Strain, break, 2 mm/min; ISO 178 | |
| 77.8 % | 77.8 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 3.4 % | 3.4 % | 5 mm/min; ISO 527 |
| 3.5 % | 3.5 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 2.52 GPa | 365 ksi | 1 mm/min; ISO 527 |
| 2.57 GPa | 373 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 72.0 MPa | 10400 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Yield Strength | 73.0 MPa | 10600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 75.0 MPa | 10900 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 2.43 GPa | 352 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 2.60 GPa | 377 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 5.30 J/cm | 9.93 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 45.0 kJ/m² | 21.4 ft-lb/in² | 80*10*4; ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 66.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
36.8 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 75.9 µm/m-°C @Temperature -40.0 - 40.0 °C |
42.2 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 96.0 °C @Thickness 3.20 mm |
205 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 2.8 @Frequency 1.00e+9 Hz |
2.8 @Frequency 1.00e+9 Hz |
ASTM D150 |
| Dissipation Factor | 0.0030 @Frequency 1.00e+9 Hz |
0.0030 @Frequency 1.00e+9 Hz |
ASTM D150 |
Users viewing this material also viewed the following:
- Precision Polymer Engineering Z75R Hydrogenated NBR Compound
- PolyOne Geon™ Vinyl Flexible A75M1 Trans 9000 Polyvinyl Chloride, Flexible (PVC, Flexible)
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 45 PHR Hi-Sil 233 Filler
- GrafTech P2 PET Film
- LATI Latene® 7H2W T-V0 PP Homopolymer, Mineral Reinforced, Heat Stabilized, Flame Retardant
- Kostat ICP-STAT ICS-1000 PC Sheet
- SABIC Innovative Plastics LNP THERMOCOMP 9H1100C
- Teknor Apex Telcar® TL-1000-105 Thermoplastic Elastomer
- A. Schulman POLYBATCH™ Yellow P20199/2 Concentrate Based In Copolymer PP
- Aremco Pyro-Paint™ 634-ZO High Temperature Refractory Coating, ZO >95%
Copyright © lookpolymers.com All Rights Reserved