SABIC Innovative Plastics LNP THERMOCOMP LF006E PEEK
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP LF006E PEEK.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* LF006E is a compound based on Polyetheretherketone resin containing 30% Glass Fiber. Added features of this material include: Easy Molding.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.53 g/cc | 0.0553 lb/in³ | ASTM D792 |
| 1.53 g/cc | 0.0553 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.0800 % | 0.0800 % | 50% RH, 24 hrs; ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 181 MPa | 26300 psi | ASTM D638 |
| 187 MPa | 27100 psi | ISO 527 | |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| 2.0 % | 2.0 % | ISO 527 | |
| Tensile Modulus | 12.9 GPa | 1870 ksi | 1 mm/min; ISO 527 |
| 13.03 GPa | 1890 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 262 MPa | 38000 psi | ASTM D790 |
| 278 MPa | 40300 psi | ISO 178 | |
| Flexural Modulus | 11.03 GPa | 1600 ksi | ASTM D790 |
| 12.5 GPa | 1810 ksi | ISO 178 | |
| Izod Impact, Notched | 1.17 J/cm | 2.19 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 9.13 J/cm | 17.1 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 11.0 kJ/m² | 5.23 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 58.0 kJ/m² | 27.6 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 8.00 J | 5.90 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 19.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
11.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 20.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
11.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 36.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
20.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 36.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
20.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | >= 240 °C | >= 464 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| >= 298 °C @Thickness 3.20 mm |
>= 568 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 240 °C | >= 464 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| >= 298 °C @Thickness 3.20 mm |
>= 568 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Multibase SILASTIC® C7-4550 CADOX BSD Dow-Corning Biomedical Grade ETR Elastomer
- ExxonMobil Santoprene® 121-65W233 Thermoplastic Elastomer (discontinued **)
- Huntsman Araldite GT 6450 Bisphenol A Epoxy Solid Resin
- ICO Polymers ICORENEâ„¢ 150-1334 LMDPE Rotational Molding Resin
- SABIC Innovative Plastics Valox® HX420HP PBT
- Zotefoams Plastazote® LD24FM Low Density Polyethylene Foam, Flame Retarded
- A. Schulman POLYFORT™ FPP 1182 Talc Fortified Impact Resistant Polypropylene
- Cytec Thornel® Mat VMC Carbon Fiber
- BASF Ultramid® 8202 PA6 (Dry)
Copyright © lookpolymers.com All Rights Reserved