SABIC Innovative Plastics LNP THERMOCOMP LCF62E PEEK
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP LCF62E PEEK.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* LCF62E is a compound based on Polyetheretherketone resin containing 10% Carbon, 30% Glass Fiber fillers. Added features of this material includes: Easy Molding, Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.57 g/cc | 1.57 g/cc | ASTM D792 |
| Density | 1.57 g/cc | 0.0567 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0200 % | 0.0200 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0200 % | 0.0200 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.00090 - 0.020 cm/cm @Time 86400 sec |
0.00090 - 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 196 MPa | 28400 psi | 5 mm/min; ISO 527 |
| 203 MPa | 29400 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 0.70 % | 0.70 % | 5 mm/min; ISO 527 |
| 0.80 % | 0.80 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 41.09 GPa | 5960 ksi | 1 mm/min; ISO 527 |
| 62.98 GPa | 9134 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 296 MPa | 42900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 391 MPa | 56700 psi | ISO 178 | |
| Flexural Modulus | 17.34 GPa | 2515 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 36.49 GPa | 5292 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.800 J/cm | 1.50 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 7.11 J/cm | 13.3 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 47.0 kJ/m² | 22.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 17.0 J @Temperature 23.0 °C |
12.5 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 290 °C | 554 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 290 °C @Thickness 3.20 mm |
554 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 290 °C | 554 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 290 °C @Thickness 3.20 mm |
554 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable 1104L-xx61FRD Polyvinyl Chloride, Flexible (PVC, Flexible)
- RheTech Products FT5100-00 Thermoplastic Polyolefin, Non-UV Stabilized, Natural
- RheTech Products G20P100-01 20% Glass Fiber Reinforced Polypropylene, Black
- Johnson Matthey Matti-sil 453S Cadmium Free Brazing Alloy
- Momentive Performance Materials Siloprenâ„¢ FSL 7651 Fluorinated Liquid Silicone Rubber
- Haynes Ultimet® alloy, aged 1000 hours at 760°C (1400°F)
- Shin-Etsu Silicones 541 Fluid
- Tipco Tipcolite® THD 311 Phenolic Compound, Wood Flour, having Medium Flow & High Strength
- ExxonMobil Bicor® 110 ASB-X OPP Film
- Aclo Accutech ABS ABS832G30L Glass Reinforced
Copyright © lookpolymers.com All Rights Reserved