SABIC Innovative Plastics LNP THERMOCOMP KFB11 Acetal Copoly (Asia Pacific)

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Glass Bead Filled
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP THERMOCOMP KFB11 Acetal Copoly (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Thermocomp* KFB11 is a compound based on Acetal Copolymer resin containing Glass Fiber, Milled Glass. Added features of this material include: Low Warpage, Chemically Coupled.
Physical Properties Metric English Comments
Density 1.48 g/cc
0.0535 lb/in³
ASTM D792
1.48 g/cc
0.0535 lb/in³
ISO 1183
Moisture Absorption 0.200 %
0.200 %
50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.019 cm/cm

@Time 86400 sec
 0.019 in/in

@Time 24.0 hour
 ISO 294
>= 0.020 cm/cm

@Time 86400 sec
 >= 0.020 in/in

@Time 24.0 hour
 ASTM D955
Linear Mold Shrinkage, Transverse 0.017 cm/cm

@Time 86400 sec
 0.017 in/in

@Time 24.0 hour
 ISO 294
0.010 - 0.030 cm/cm

@Time 86400 sec
 0.010 - 0.030 in/in

@Time 24.0 hour
 ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 60.0 MPa
8700 psi
ISO 527
62.0 MPa
8990 psi
ASTM D638
Tensile Strength, Yield 64.0 MPa
9280 psi
ASTM D638
65.0 MPa
9430 psi
ISO 527
Elongation at Break 5.7 %
5.7 %
ASTM D638
7.0 %
7.0 %
ISO 527
Elongation at Yield 3.9 %
3.9 %
ISO 527
4.0 %
4.0 %
ASTM D638
Tensile Modulus 4.10 GPa
595 ksi
1 mm/min; ISO 527
4.13 GPa
599 ksi
50 mm/min; ASTM D638
Flexural Strength 91.0 MPa
13200 psi
ISO 178
Flexural Modulus 3.00 GPa
435 ksi
ISO 178
3.44 GPa
499 ksi
ASTM D790
Izod Impact, Notched 0.530 J/cm
0.993 ft-lb/in
ASTM D256
Izod Impact, Unnotched 5.28 J/cm
9.89 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 5.00 kJ/m²
2.38 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 35.0 kJ/m²
16.7 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 6.00 J
4.43 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 1.00 J
0.738 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 107 µm/m-°C

@Temperature -40.0 - 40.0 °C
 59.4 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
108 µm/m-°C

@Temperature -40.0 - 40.0 °C
 60.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
CTE, linear, Transverse to Flow 86.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 47.8 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
86.4 µm/m-°C

@Temperature -40.0 - 40.0 °C
 48.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 161 °C
322 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
162 °C

@Thickness 3.20 mm
 324 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 150 °C
302 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
152 °C

@Thickness 3.20 mm
 306 °F

@Thickness 0.126 in
 unannealed; ASTM D648