SABIC Innovative Plastics LNP THERMOCOMP KF004 Acetal Copolymer (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, 20% Glass Fiber Reinforced
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP THERMOCOMP KF004 Acetal Copolymer (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* THERMOCOMP* KF004 is a compound based on Acetal Copolymer containing Glass Fiber. Added features include : Chemically Coupled.
Physical Properties Metric English Comments
Density 1.54 g/cc
0.0556 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0050 cm/cm
0.0050 in/in
SABIC Method
Mechanical Properties Metric English Comments
Tensile Strength at Break 104 MPa
15100 psi
5 mm/min; ISO 527
Elongation at Yield 2.3 %
2.3 %
5 mm/min; ISO 527
Tensile Modulus 7.20 GPa
1040 ksi
1 mm/min; ISO 527
Flexural Yield Strength 122 MPa
17700 psi
2 mm/min; ISO 178
Flexural Modulus 5.50 GPa
798 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 7.00 kJ/m²
3.33 ft-lb/in²
80*10*4; ISO 180/1A
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 63.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 35.0 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 107 µm/m-°C

@Temperature 23.0 - 60.0 °C
 59.4 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 157 °C
315 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af