SABIC Innovative Plastics LNP THERMOCOMP JF002 PES
| Category | Polymer , Thermoplastic , Polyethersulfone (PES) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP JF002 PES.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* JF002 is a compound based on Polyethersulfone resin containing 10% Glass Fiber.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in³ | ASTM D792 |
| 1.45 g/cc | 0.0524 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.510 % | 0.510 % | 50% RH, 24 hrs; ASTM D570 |
| 0.850 % | 0.850 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm @Time 86400 sec |
0.0040 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0070 cm/cm @Time 86400 sec |
0.0050 - 0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 102 MPa | 14800 psi | Type I, 5 mm/min; ASTM D638 |
| 102 MPa | 14800 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 103 MPa | 14900 psi | 5 mm/min; ISO 527 |
| 105 MPa | 15200 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 5.0 % | 5.0 % | 5 mm/min; ISO 527 |
| 5.4 % | 5.4 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 4.3 % | 4.3 % | 5 mm/min; ISO 527 |
| 4.4 % | 4.4 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 4.42 GPa | 641 ksi | 1 mm/min; ISO 527 |
| 4.68 GPa | 679 ksi | 50 mm/min; ASTM D638 | |
| Flexural Yield Strength | 176 MPa | 25500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 4.06 GPa | 589 ksi | 2 mm/min; ISO 178 |
| 4.37 GPa | 634 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.530 J/cm | 0.993 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.39 J/cm | 15.7 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 54.0 kJ/m² | 25.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 37.1 µm/m-°C @Temperature -30.0 - 30.0 °C |
20.6 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 44.1 µm/m-°C @Temperature -30.0 - 30.0 °C |
24.5 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 221 °C | 430 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 220 °C @Thickness 3.20 mm |
428 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 212 °C | 414 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 214 °C @Thickness 3.20 mm |
417 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Pyrotek F-24 Dense Machinable Board
- Hogen Duralloy H5TC 50 Tungsten Carbide/50 Copper PM Metal Composite
- Ineos ABS Lustran® 130
- Iran Petrochemical (PCC) EX 2 S HF 7750 M2 High Density Polyethylene
- Momentive Performance Materials RTV5243 Neutral Cure, One Component RTV Adhesive Sealant
- SABIC Innovative Plastics LNP LUBRICOMP OCP36 PPS
- Westlake Plastics HIPS High Impact Polystyrene
- ATI Allegheny Ludlum Stainless Steel Chromium-Nickel Type 305, Annealed (UNS S30500)
Copyright © lookpolymers.com All Rights Reserved