SABIC Innovative Plastics LNP THERMOCOMP IF003 PA 6/12
| Category | Polymer , Thermoplastic , Nylon , Nylon 612 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP IF003 PA 6/12.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* IF003 is a compound based on Nylon 6/12 resin containing 15% Glass Fiber.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.17 g/cc | 0.0423 lb/in³ | ISO 1183 |
| 1.18 g/cc | 0.0426 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.220 % | 0.220 % | 50% RH, 24 hrs; ASTM D570 |
| 0.260 % | 0.260 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm @Time 86400 sec |
0.0040 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0040 - 0.0060 cm/cm @Time 86400 sec |
0.0040 - 0.0060 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.011 cm/cm @Time 86400 sec |
0.010 - 0.011 in/in @Time 24.0 hour |
ISO 294 |
| 0.010 - 0.012 cm/cm @Time 86400 sec |
0.010 - 0.012 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 99.0 MPa | 14400 psi | ISO 527 |
| 100 MPa | 14500 psi | ASTM D638 | |
| Elongation at Break | 2.1 % | 2.1 % | ISO 527 |
| 2.6 % | 2.6 % | ASTM D638 | |
| Tensile Modulus | 5.43 GPa | 788 ksi | 1 mm/min; ISO 527 |
| 5.53 GPa | 802 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 156 MPa | 22600 psi | ISO 178 |
| 163 MPa | 23600 psi | ASTM D790 | |
| Flexural Modulus | 4.59 GPa | 666 ksi | ISO 178 |
| 5.21 GPa | 756 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.420 J/cm | 0.787 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.40 J/cm | 4.50 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 22.0 kJ/m² | 10.5 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 6.00 J | 4.43 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 45.1 µm/m-°C @Temperature -40.0 - 40.0 °C |
25.1 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 45.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
25.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 80.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
44.7 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 80.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
44.7 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 181 °C | 358 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 191 °C @Thickness 3.20 mm |
376 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Precision Polymer Engineering N80V Nitrile Rubber
- PolyOne Geon™ Vinyl Flexible D80M0 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Loxim 220 01V0 Polybutylene Terephthalate
- Kostat ICP-STAT ICD-1005 ABS Sheet
- Techmer ES HiFill FR® PC FR HS GY154
- Formosa Plastics Formolene® L42009M Film (Butene Grade) LLDPE
- Crucible Steel REX® TMO High Speed Steel, AISI M1
- ExxonMobil 846 Mobil DTE 800 Series
- Eurotec® Tecolen® HP30 KG30 NL HS 0B PPCP, 30% glass fiber/glass bead reinforced, heat stabilized, natural
- PolyOne LubriOne™ ATH-000/10T 2S Acetal (POM) Homopolymer (discontinued **)
Copyright © lookpolymers.com All Rights Reserved