SABIC Innovative Plastics LNP THERMOCOMP HH0420A PA11

Category Polymer , Thermoplastic , Nylon , Nylon 11
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP THERMOCOMP HH0420A PA11.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* THERMOCOMP* HH0420A is a compound based on Nylon 11 containing proprietary fillers. Added features of this material are High Specific Gravity.
Physical Properties Metric English Comments
Specific Gravity 4.30 g/cc
4.30 g/cc
ASTM D792
Density 4.28 g/cc
0.155 lb/in³
ASTM D792
Moisture Absorption 0.0200 %
0.0200 %
50% RH, 24 hrs; ASTM D570
0.0300 %
0.0300 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0070 - 0.0090 cm/cm

@Time 86400 sec
 0.0070 - 0.0090 in/in

@Time 24.0 hour
 ASTM D955
Linear Mold Shrinkage, Transverse 0.0070 - 0.0090 cm/cm

@Time 86400 sec
 0.0070 - 0.0090 in/in

@Time 24.0 hour
 ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 40.0 MPa
5800 psi
Type I, 5 mm/min; ASTM D638
41.0 MPa
5950 psi
5 mm/min; ISO 527
Tensile Strength, Yield 40.0 MPa
5800 psi
Type I, 5 mm/min; ASTM D638
41.0 MPa
5950 psi
5 mm/min; ISO 527
Elongation at Break 1.3 %
1.3 %
Type I, 5 mm/min; ASTM D638
1.4 %
1.4 %
5 mm/min; ISO 527
Elongation at Yield 1.3 %
1.3 %
Type I, 5 mm/min; ASTM D638
1.4 %
1.4 %
5 mm/min; ISO 527
Tensile Modulus 4.84 GPa
702 ksi
1 mm/min; ISO 527
5.77 GPa
837 ksi
50 mm/min; ASTM D638
Flexural Strength 61.0 MPa
8850 psi
1.3 mm/min, 50 mm span; ASTM D790
62.0 MPa
8990 psi
ISO 178
Flexural Yield Strength 61.0 MPa
8850 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 4.77 GPa
692 ksi
2 mm/min; ISO 178
4.88 GPa
708 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.330 J/cm
0.618 ft-lb/in
ASTM D256
Izod Impact, Unnotched 2.02 J/cm
3.78 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 6.00 kJ/m²
2.86 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 13.0 kJ/m²
6.19 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 9.00 J

@Temperature 23.0 °C
 6.64 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Impact Test 1.00 J
0.738 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.44
0.44
ASTM D3702 Modified
Coefficient of Friction, Static 0.38
0.38
ASTM D3702 Modified
K (wear) Factor 96.7 x 10-8 mm³/N-M
48.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 66.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
 36.7 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D696
CTE, linear, Transverse to Flow 65.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
 36.1 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 167 °C
333 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
162 °C

@Thickness 3.20 mm
 324 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 95.0 °C
203 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
84.0 °C

@Thickness 3.20 mm
 183 °F

@Thickness 0.126 in
 unannealed; ASTM D648