SABIC Innovative Plastics LNP THERMOCOMP EFB26ER PEI (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP EFB26ER PEI (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* EFB26ER is a compound based on Polyetherimide containing Glass Fiber, Glass Bead. Added features include: Easy Molding, Mold Release.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.61 g/cc | 0.0582 lb/in³ | ISO 1183 |
| Water Absorption | 0.27 % @Time 86400 sec |
0.27 % @Time 24.0 hour |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm | 0.0020 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 153 MPa | 22200 psi | 5 mm/min; ISO 527 |
| Tensile Strength, Yield | 156 MPa | 22600 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 1.5 % | 1.5 % | 5 mm/min; ISO 527 |
| 1.9 % | 1.9 % | Flexural Strain, break, 2 mm/min; ISO 178 | |
| Elongation at Yield | 1.5 % | 1.5 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 9.00 GPa | 1310 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 190 MPa | 27600 psi | 2 mm/min; ISO 178 |
| Flexural Yield Strength | 190 MPa | 27600 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 10.4 GPa | 1510 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 25.0 kJ/m² | 11.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 15.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
8.33 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 35.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
19.4 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 206 °C | 403 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
Users viewing this material also viewed the following:
- Radici Heraflex® A 60 31 I HS1 TPS-SEBS Thermoplastic Elastomer
- Hong Kun Group HBCD Flame Retardant
- LyondellBasell Microthene® F FA70900 High Density Polyethylene
- Taiwan PU Corporation TPUI-T85 Transparent Grade, Injection Molding Polyester Base TPU
- Universal Wire Works Inconel 92 (AMS 5675) Nickel Alloy Filler Metal
- Borealis RG435MO Polypropylene, Transparent Random Copolymer
- ExxonMobil Exxtral™ BMV 208 Performance Polyolefin
- Dow AFFINITY™ SM 8400 Polyolefin Elastomer
- Beijing Evergrow Resources UHF-BF1500 UHMW PE Fiber
Copyright © lookpolymers.com All Rights Reserved