| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | EXW, FOB, CFR, CIF |
| Payment Terms | L/C, T/T, PayPal |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP DX07350 PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Lexan *DX07350 resin is a glass filled, Non-brominated & Non-chlorinated flame retardant polycarbonate. High stiffness and good flow.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.29 g/cc | 1.29 g/cc | ASTM D792 |
| Density | 1.29 g/cc | 0.0466 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.0500 % | 0.0500 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.090 % | 0.090 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0035 - 0.0045 cm/cm <br>@Thickness 3.20 mm |
0.0035 - 0.0045 in/in <br>@Thickness 0.126 in |
SABIC Method |
| Melt Index of Compound | 21 g/10 min <br>@Load 2.16 kg,<br> Temperature 280 °C |
21 g/10 min <br>@Load 4.76 lb,<br> Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 54.0 MPa | 7830 psi | 5 mm/min; ISO 527 |
| 55.0 MPa | 7980 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 65.0 MPa | 9430 psi | Type I, 5 mm/min; ASTM D638 |
| 68.0 MPa | 9860 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 4.8 % | 4.8 % | 5 mm/min; ISO 527 |
| 5.0 % | 5.0 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 3.8 % | 3.8 % | 5 mm/min; ISO 527 |
| 4.0 % | 4.0 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 4.70 GPa | 682 ksi | 5 mm/min; ASTM D638 |
| 4.80 GPa | 696 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 116 MPa | 16800 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 120 MPa | 17400 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 4.20 GPa | 609 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 4.60 GPa | 667 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.420 J/cm | 0.787 ft-lb/in | ASTM D256 |
| 0.350 J/cm <br>@Temperature -30.0 °C |
0.656 ft-lb/in <br>@Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*3; ISO 180/1A |
| 4.00 kJ/m² <br>@Temperature -30.0 °C |
1.90 ft-lb/in² <br>@Temperature -22.0 °F |
80*10*3; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 50.0 kJ/m² | 23.8 ft-lb/in² | 80*10*3; ISO 180/1U |
| 47.0 kJ/m² <br>@Temperature -30.0 °C |
22.4 ft-lb/in² <br>@Temperature -22.0 °F |
80*10*3; ISO 180/1U | |
| Charpy Impact Unnotched | 7.50 J/cm² | 35.7 ft-lb/in² | Edgew 80*10*3 sp=62mm; ISO 179/1eU |
| 6.10 J/cm² <br>@Temperature -30.0 °C |
29.0 ft-lb/in² <br>@Temperature -22.0 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 0.300 J/cm² | 1.43 ft-lb/in² | Edgew 80*10*3 sp=62mm; ISO 179/1eA |
| 0.300 J/cm² <br>@Temperature -30.0 °C |
1.43 ft-lb/in² <br>@Temperature -22.0 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eA | |
| Dart Drop, Total Energy | 11.0 J <br>@Temperature 23.0 °C |
8.11 ft-lb <br>@Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 37.0 µm/m-°C <br>@Temperature -40.0 - 40.0 °C |
20.6 µin/in-°F <br>@Temperature -40.0 - 104 °F |
ASTM E 831 |
| 37.0 µm/m-°C <br>@Temperature -40.0 - 40.0 °C |
20.6 µin/in-°F <br>@Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 66.0 µm/m-°C <br>@Temperature -40.0 - 40.0 °C |
36.7 µin/in-°F <br>@Temperature -40.0 - 104 °F |
ASTM E 831 |
| 66.0 µm/m-°C <br>@Temperature -40.0 - 40.0 °C |
36.7 µin/in-°F <br>@Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 104 °C | 219 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 102 °C <br>@Thickness 3.20 mm |
216 °F <br>@Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 109 °C | 228 °F | Rate B/50; ISO 306 |
| 112 °C | 234 °F | Rate B/120; ISO 306 | |
| 112 °C | 234 °F | Rate B/50; ASTM D1525 | |
| Flammability, UL94 | V-0 <br>@Thickness 0.800 mm |
V-0 <br>@Thickness 0.0315 in |
UL 94 by SABIC-IP |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Pencil Hardness test, 0.5 kgf | F | ASTM D3363 |
| Pencil Hardness test, 1kgf | HB | ASTM D3363 |
Users viewing this material also viewed the following:
- PolyOne Maxxam™ FR WC-P85 NHFR RoHS Natural Polyolefin, Unspecified
- SABIC Innovative Plastics Lexan® RL7517 PC
- Michelman® Michem® Shield 422 Anionic dispersion of polyethylene wax
- Hong Kun Group 4-Methyl-2-nitrobenzonitrile Pharmaceutical Intermediate
- Multibase Multi-Flex® A 6041 Clear TPE Thermoplastic Elastomer
- DuPont Performance Polymers Zytel® HTN FR52G45BL BK337 Polyphthalamide (PPA) (Unverified Data**)
- Colorite Polymers 8500 General Purpose Vinyl Compound
- ATG s.r.l. EPM Ethylene-Propylene Copolymer
- Amity Thermosets ATG 112 Phenolic Molding Organic Filler, Compression Molded
- Mateck Zero Expansion Glass - ZERODUR
Copyright © lookpolymers.com All Rights Reserved