SABIC Innovative Plastics LNP THERMOCOMP DX05475 PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP DX05475 PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* DX05474 is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Flame Retardant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.29 g/cc | 0.0466 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0040 cm/cm @Time 86400 sec |
0.0030 - 0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 54.0 MPa | 7830 psi | ASTM D638 |
| Tensile Strength, Yield | 59.0 MPa | 8560 psi | ASTM D638 |
| Elongation at Break | 8.2 % | 8.2 % | ASTM D638 |
| Elongation at Yield | 4.9 % | 4.9 % | ASTM D638 |
| Tensile Modulus | 3.59 GPa | 521 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 103 MPa | 14900 psi | ASTM D790 |
| Flexural Modulus | 3.61 GPa | 524 ksi | ASTM D790 |
| Izod Impact, Notched | 0.580 J/cm | 1.09 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 10.68 J/cm | 20.01 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 132 °C @Thickness 3.20 mm |
270 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- SABIC F01552 High Density Polyethylene for Blown Film
- Polykemi AB POLYabs T00 ABS, Transparent
- Overview of materials for Ethylene Vinyl Acetate Copolymer (EVA), Extrusion/Coating Grade
- Karina E 856-08/151-Y-ERYB Beige PVC Compound
- Lubrizol Estane® 2355-75A Thermoplastic Polyurethane Elastomer
- Esstech X-733-7446 1,12 Dodecanediol Dimethacrylate, C20H34O4
- Arlon 18609R023 0.023" (0.584 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- Nye Lubricants 762G (NG) Synthetic Oil
- ExxonMobil Mobil 1 75W-140 Gear Lubricant LS
Copyright © lookpolymers.com All Rights Reserved