SABIC Innovative Plastics LNP THERMOCOMP DF002ERJ PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP DF002ERJ PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* DF002ERJ is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Easy Molding, Healthcare.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in³ | ISO 1183 |
| 1.275 g/cc | 0.04606 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.150 % | 0.150 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm @Time 86400 sec |
0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0043 cm/cm @Time 86400 sec |
0.0043 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0050 cm/cm @Time 86400 sec |
0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0051 cm/cm @Time 86400 sec |
0.0051 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 83.0 MPa | 12000 psi | ASTM D638 |
| 84.0 MPa | 12200 psi | ISO 527 | |
| Elongation at Break | 3.6 % | 3.6 % | ISO 527 |
| 3.8 % | 3.8 % | ASTM D638 | |
| Tensile Modulus | 4.10 GPa | 595 ksi | 1 mm/min; ISO 527 |
| 4.17 GPa | 605 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 117 MPa | 17000 psi | ISO 178 |
| 149 MPa | 21600 psi | ASTM D790 | |
| Flexural Modulus | 3.92 GPa | 569 ksi | ISO 178 |
| 4.28 GPa | 621 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.970 J/cm | 1.82 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 9.29 J/cm | 17.4 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 61.0 kJ/m² | 29.0 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 13.0 J | 9.59 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 9.00 J | 6.64 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 38.1 µm/m-°C @Temperature -40.0 - 40.0 °C |
21.2 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 38.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
21.2 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 53.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
29.7 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 53.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
29.7 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 141 °C | 286 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 141 °C @Thickness 3.20 mm |
286 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 137 °C | 279 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 136 °C @Thickness 3.20 mm |
277 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Huntsman AVALON® 55 AEX Thermoplastic Polyurethane
- LG Chemical LUCEL WK-320 Wear Resistant POM, 20% Mineral Filled, High Modulus
- Michelman® FiberMax® 5000 Water based medium treatment to replace paraffin wax
- Momentive Performance Materials Siloprenâ„¢ LSR 2661 Liquid Silicone Rubber - Non Post Cure / Low Compression Set
- Sylvin Technologies 8950-80 Natural PVC Extrusion Compound
- A. Schulman PP 1329H-01 Polypropylene Medium Impact Polypropylene
- ELASTO UK Dryflex® 600800S SEBS Based Material, Filled Qualities, 80A Hardness, Natural
- DuPont Performance Polymers Zytel® 73G15L NC010 Nylon 6 (Unverified Data**)
- Arlon 55638R030 0.030" (0.762 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- Abatron AboCast 8110-5/AboCure 8110-1 Flexible Epoxy
Copyright © lookpolymers.com All Rights Reserved