SABIC Innovative Plastics LNP THERMOCOMP DF002ER PC (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP DF002ER PC (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* DF002ER is a compound based on Polycarbonate resin containing Glass Fiber. Added features include Easy Molding, Mold Release.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 85.0 MPa | 12300 psi | 5 mm/min; ISO 527 |
| Elongation at Yield | 3.6 % | 3.6 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 4.00 GPa | 580 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 135 MPa | 19600 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 3.80 GPa | 551 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 50.0 kJ/m² | 23.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 39.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
21.7 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 143 °C | 289 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 137 °C | 279 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Flammability, UL94 | V-2 @Thickness 1.50 mm |
V-2 @Thickness 0.0591 in |
UL 94 |
| V-1 @Thickness 3.00 mm |
V-1 @Thickness 0.118 in |
UL 94 | |
| Glow Wire Test | 850 °C @Thickness 1.60 mm |
1560 °F @Thickness 0.0630 in |
IEC 60695-2-12 |
| 960 °C @Thickness 1.00 mm |
1760 °F @Thickness 0.0394 in |
IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 175 V | 175 V | IEC 60112 |
Users viewing this material also viewed the following:
- Huntsman Araldite GY 9615 Bisphenol A Epoxy Liquid Resin
- M. Holland Company CP710 Polypropylene Impact Copolymer
- MarkeTech BGO (Bismuth Germanate, Bi4Ge3O12) Scintillator Crystal
- Gwent Electronic Materials C2030701D3 Solderable Silver Ink
- SABIC Innovative Plastics ULTEM 2312EPR PEI
- A. Schulman POLYBATCH™ Blue 40460/4 Concentrate Based In LLDPE
- A. Schulman CP851 High Flow, Injection Molding Grade
- Arlon 47581R007 0.007" (0.178 mm) Uncured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved