SABIC Innovative Plastics LNP THERMOCOMP D452 PC COPOLYMER (Asia Pacific)

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP THERMOCOMP D452 PC COPOLYMER (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Thermocomp* D452 (or EXTC8202) is a compound based on SABIC unique Polycarbonate copolymer resin containing Glass Fiber, Flame Retardant. Added features of this material include: High modulus, good flatness, good ductility, Non-Brominated & Non-Chlorinated Flame Retardant, and super good flow with IMR/IMD capability.
Physical Properties Metric English Comments
Density 1.52 g/cc
0.0549 lb/in³
ASTM D792
Linear Mold Shrinkage, Flow 0.0010 - 0.0025 cm/cm

@Time 86400 sec
 0.0010 - 0.0025 in/in

@Time 24.0 hour
 ASTM D955
Linear Mold Shrinkage, Transverse 0.0010 - 0.0025 cm/cm

@Time 86400 sec
 0.0010 - 0.0025 in/in

@Time 24.0 hour
 ASTM D955
Melt Flow 17.4 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 17.4 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 ASTM D1238
39 g/10 min

@Load 2.16 kg,
Temperature 300 °C
 39 g/10 min

@Load 4.76 lb,
Temperature 572 °F
 ASTM D1238
Melt Index of Compound 12 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 12 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 MVR [cm^3/10 min]; ISO 1133
30 g/10 min

@Load 2.16 kg,
Temperature 300 °C
 30 g/10 min

@Load 4.76 lb,
Temperature 572 °F
 MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 140 MPa
20300 psi
5 mm/min; ISO 527
141 MPa
20500 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 2.2 %
2.2 %
5 mm/min; ISO 527
2.3 %
2.3 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 11.29 GPa
1637 ksi
1 mm/min; ISO 527
11.96 GPa
1735 ksi
5 mm/min; ASTM D638
Flexural Strength 211 MPa
30600 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Yield Strength 189 MPa
27400 psi
2 mm/min; ISO 178
Flexural Modulus 10.05 GPa
1458 ksi
2 mm/min; ISO 178
11.66 GPa
1691 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 1.45 J/cm
2.72 ft-lb/in
ASTM D256
Izod Impact, Unnotched 6.20 J/cm
11.6 ft-lb/in
ASTM D4812
Charpy Impact Unnotched 4.10 J/cm²
19.5 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eU
Charpy Impact, Notched 1.30 J/cm²
6.19 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 15.8 µm/m-°C

@Temperature 23.0 - 80.0 °C
 8.78 µin/in-°F

@Temperature 73.4 - 176 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 58.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
 32.2 µin/in-°F

@Temperature 73.4 - 176 °F
 ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 98.0 °C

@Thickness 3.20 mm
 208 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Flammability, UL94 V-0

@Thickness 1.00 mm
 V-0

@Thickness 0.0394 in
 UL 94