IRPC Polimaxx Polene 2311KX TA4 Polypropylene Compound
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | IRPC Polimaxx |
| Trade Name | Polene |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | IRPC Polimaxx Polene 2311KX TA4 Polypropylene Compound.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
CHARACTERISTICS: POLYPROPYLENE BLOCK COPOLYMER WITH 20% TALCUM REINFORCED, HIGH IMPACT STRENGTHAPPLICATIONS: INJECTION MOLDING FOR AUTOPARTS, ELECTRICAL APPLIANCES
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ASTM D792 |
| Melt Flow | 4.5 g/10 min @Load 2.16 kg, Temperature 230 °C |
4.5 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 102 | 102 | ASTM D785 |
| Tensile Strength, Yield | 32.9 MPa | 4770 psi | ASTM D638 |
| Elongation at Break | 20 % | 20 % | ASTM D638 |
| Flexural Yield Strength | 46.1 MPa | 6680 psi | ASTM D790 |
| Flexural Modulus | 3.10 GPa | 450 ksi | ASTM D790 |
| Izod Impact, Notched | 0.471 J/cm @Temperature 23.0 °C |
0.882 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 140 °C | 284 °F | ASTM D648 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® 4701R PPC
- Kraton® D1101 K (SBS) Liner Block Copolymer
- LyondellBasell Lupolen® 1810 E LDPE
- SABIC Innovative Plastics LNP Thermocomp RF0057E PA 66 (Asia Pacific)
- BASF Neopolen® P 9230 D 0.05 g/cc Core density; Expanded Polypropylene (Europe)
- Applied Composites 8049 Polyester SMC
- DSM Akulon® F130-B Nylon 6 (European Grade) (Dry) (discontinued **)
- Karina 802-10/93-AY-ERYB White PVC Compound
Copyright © lookpolymers.com All Rights Reserved