ACC EP 2KSP EPI Engineered Polymers Silicone Modified Polyurea
| Category | Polymer , Thermoset , Silicone |
| Manufacturer | Amber Chemical Company |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ACC EP 2KSP EPI Engineered Polymers Silicone Modified Polyurea.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
EP 2KSP Polyurea, “Powered by Reactamine® Technology”, is a 2 Component polyurea that reacts with aliphatic isocyanates to produce a high gloss, chemical resistant coating EP 2KSP can be used on a variety of substrates such as bed liners, concrete, wood, metal and plastic for interior and exterior applications. EP 2KSP should be sprayed on bed liners, but can be rolled or sprayed on other surfaces at about 3-4 mils. Key Benefits include: High gloss, Excellent chemical resistance, Quick drying, Excellent surface hardness, Excellent compatibility with polyurethane dispersions and other acrylic emulsions. Coalescing Solvents: Butyl glycol, Butyl diglycol, Dowanol DPM, Dowanol PM, Dowanol DPnB, Dowanol TPnB, Dowanol PnB, propylene glycol butyl-acetate, Propylene glycol, NMP, Methoxybutanol, Ethanol, Lusolvan FBH, Proglide DMM. Part of the Amber Chemical Group. Data provided by manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.143 g/cc | 0.00516 lb/in³ | |
| 1.07 g/cc | 0.0387 lb/in³ | ||
| Solids Content | 35 % | 35 % | |
| pH | 7.5 - 8.5 | 7.5 - 8.5 | |
| Brookfield Viscosity | 40 - 100 cP | 40 - 100 cP | RVT, Spindle 2, 20 rpm |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Abrasion | 4.7 | 4.7 | mg loss |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 17.0 °C | 62.6 °F | Minimum Film Formation Temperature |
| Cure Time | <= 60.0 min @Thickness 0.152 mm, Temperature 75.0 °C |
<= 1.00 hour @Thickness 0.00600 in, Temperature 167 °F |
|
| Pot Life | <= 60 min | <= 60 min |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Clear | |
| Hot Tire | No Stain | |
| Plasticizer (1 hour) | 5 | 0 (Failure)-5 (Excellent) |
| Resistance to Acetone (10 seconds) | 5 | 0 (Failure)-5 (Excellent) |
| Resistance to Alcohol (1 hour) | 4 | 0 (Failure)-5 (Excellent) |
| Resistance to Alcohol/Water 1:1 (1 hour) | 5 | 0 (Failure)-5 (Excellent) |
| Resistance to Ammonia (1 hour) | 5 | 0 (Failure)-5 (Excellent) |
| Resistance to Brake Fluid (2 hours) | No effect | |
| Resistance to Brake Fluid (24 hours) | 0 | 0 (Failure)-5 (Excellent) |
| Resistance to Coffee (16 hours) | 5 | 0 (Failure)-5 (Excellent) |
| Resistance to Diesel Fuel (24 hours) | No effect | |
| Resistance to Gasoline | No effect | |
| Resistance to Motor Oil (24 hours) | No effect | |
| Resistance to Nivea (16 hours) | 5 | 0 (Failure)-5 (Excellent) |
| Resistance to Pepsi Cola (24 hours) | No effect | |
| Resistance to Transmission Fluid (24 hours) | No effect | |
| Resistance to Water (16 hours) | 5 | 0 (Failure)-5 (Excellent) |
| Stabilization | Anionic |
Users viewing this material also viewed the following:
- NYCOA 2263 Copolymer Nylon Alloy
- MV Labs PR800 Pr6O11 Praseodymium(III,IV) oxide
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 40 PHR N774 (SRF) Filler
- Lehmann & Voss LUVOCOM® 20-0778/BK Polyphthalamide, with glass fiber and PTFE
- Entec Hypro™ PPC-GF10 Natural Impact Polypropylene, 10% Glass Reinforced
- Diamond Polymers NPP25-0504LGF40 40% Long Glass Fiber Filled Copolymer Polypropylene
- DSM Akulon® K224-G3 (Cond.) 15% Glass Reinforced Nylon 6 (North America)
- Arlon 55589W028 0.028" (0.711 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- Arlon 30580R020 0.020" (0.508 mm) Uncured Unsupported Silicone Rubber on Kodacel Carrier
- 3M 507 Sandblast Stencil
Copyright © lookpolymers.com All Rights Reserved