SABIC Innovative Plastics LNP Stat-kon PX98038 PA 6 (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Stat-kon PX98038 PA 6 (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STATKON* PX98038 is a compound based on PA6 resin containing Carbon Fiber, Glass Fiber, Flame Retardant. Added features include : Flame Retardant, Electrically Conductive, Heat Stabilized.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.47 g/cc | 0.0531 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 2.00 MPa | 290 psi | 5 mm/min; ISO 527 |
| Tensile Strength, Yield | 136 MPa | 19700 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 3.9 % | 3.9 % | Flexural Strain, 2 mm/min; ISO 178 |
| Tensile Modulus | 12.2 GPa | 1770 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 199 MPa | 28900 psi | 2 mm/min; ISO 178 |
| Flexural Yield Strength | 201 MPa | 29200 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 9.40 GPa | 1360 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² @Temperature 23.0 °C |
3.33 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 35.0 kJ/m² @Temperature 23.0 °C |
16.7 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 19.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
10.6 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 89.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
49.4 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Flammability, UL94 | V-1 @Thickness 3.00 mm |
V-1 @Thickness 0.118 in |
UL 94 by SABIC-IP |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 10000 - 1.00e+6 ohm | 10000 - 1.00e+6 ohm | ASTM D 257 |
Users viewing this material also viewed the following:
- Huntsman Araldite GT 9496 Bisphenol A Epoxy Solid Resin
- A. Schulman POLYPUR™ FPU 1550 Thermoplastic Polyurethane Compound
- CP-Polymer-Technik Wellamid® 6000 CF 18 HWCP 18% Carbon Fiber Nylon 6, Heat Stabilized, Conditioned
- Compuestos Dominicanos Polycom AU-050595 PVC Compound
- ConocoPhillips Hydroclear® MV150 AW Hydraulic Fluid
- Karina 802-27/13-IS-RG Smoky Clear PVC Compound
- Polyram RamShine PV504WT/GR Acrylonitrile Butadiene Styrene, Flame Retardant
Copyright © lookpolymers.com All Rights Reserved