Chevron Phillips Marlex® C513UV High Density Polyethylene, Blow Molding

Category	Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Blow Molding Grade
Manufacturer	Chevron Phillips Chemical Company LP
Trade Name	Marlex®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Chevron Phillips Marlex® C513UV High Density Polyethylene, Blow Molding.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

This extra high molecular weight, hexane copolymer is tailored for intermediate bulk container applications that require:Outstanding impact resistanceOutstanding ESCRExcellent processabilityUV stabilizationTypical applications for C513UV include blow molded items such as:Intermediate bulk containersAgricultural containersThis resin meets these specifications:ASTM D4976 - PE 235FDA 21 CFR 177.1520(c) 3.1a, use conditions C through G per 21 CFR 176.170(c). Volume of food containing article must be equal to or greater than 5 gallons.Information provided by Chevron Phillips Chemical Company LP.

Physical Properties	Metric	English	Comments
Specific Gravity	0.945 g/cc	0.945 g/cc	ASTM D1505
ESCR 100% Igepal®	>= 2000 hour	>= 2000 hour	Condition A, F50; ASTM D1693
	>= 2000 hour	>= 2000 hour	Condition B, F50; ASTM D1693
Melt Flow	5.5 g/10 min @Load 21.6 kg, Temperature 190 °C	5.5 g/10 min @Load 47.6 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	61	61	ASTM D2240
Tensile Strength, Yield	24.0 MPa	3480 psi	2 in/min, Type IV bar; ASTM D638
Elongation at Break	700 %	700 %	2 in/min, Type IV bar; ASTM D638
Flexural Modulus	1.07 GPa	155 ksi	Tangent; ASTM D790
Tensile Impact Strength	580 kJ/m²	276 ft-lb/in²	ASTM D1822

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	66.0 °C	151 °F	ASTM D648
Vicat Softening Point	123 °C	253 °F	ASTM D1525
Brittleness Temperature	<= -75.0 °C	<= -103 °F	Type A clamp, Type I Specimen; ASTM D746