Advanced Polymer Alloys Alcryn® 2080 BK Melt Processable Rubber

Category	Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Elastomer, Melt-Processible Rubber
Manufacturer	APA - Advanced Polymer Alloys
Trade Name	Alcryn®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Advanced Polymer Alloys Alcryn® 2080 BK Melt Processable Rubber.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Alcryn melt-processable rubber (MPR) is a true rubber, based on a partially cross-linked, chlorinated olefin interpolymer alloy. Alcryn is designed for the manufacture of rubber parts with high productivity on thermoplastic processing equipment.Applications:Window and door weatherstripping (and other complex profile extrusions)Soft handles and gripsMolded seals and gasketsInjection-molded and co-injection molded partsBlow-molded partsTubing and hoseWire and cable jacketsCoated fabrics and sheet goodsInformation provided by Advanced Polymer Alloys

Physical Properties	Metric	English	Comments
Specific Gravity	1.17 g/cc	1.17 g/cc	ASTM D471; ISO 2781
Viscosity	700000 cP @Shear Rate 300 1/s, Temperature 190 °C	700000 cP @Shear Rate 300 1/s, Temperature 374 °F	ASTM D3835

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	76	76	After 7 days at 257°F (125°C); ASTM D573; ISO 188
	78	78	ASTM D2240; ISO 48
Tensile Strength, Ultimate	11.0 MPa	1600 psi	After 7 days at 257°F (125°C); ASTM D573; ISO 188
	12.1 MPa	1760 psi	ASTM D412; ISO 37
Elongation at Break	235 %	235 %	After 7 days at 257°F (125°C); ASTM D573; ISO 188
	320 %	320 %	ASTM D412; ISO 37
100% Modulus	0.00524 GPa	0.760 ksi	After 7 days at 257°F (125°C); ASTM D573; ISO 188
	0.00627 GPa	0.910 ksi	ASTM D412; ISO 37
Graves Tear Strength	35.1 kN/m @Temperature 23.9 °C	200 pli @Temperature 75.0 °F	Die C; ASTM D624
Taber Abrasion, mg/1000 Cycles	3.0	3.0	Cs-17 Wheel, 1000 g Load; ASTM D3389
Compression Set	14 %	14 %	After 22 Hr at 75°F (24°C); ASTM D395; ISO 815
	62 % @Temperature 100 °C	62 % @Temperature 212 °F	22 hrs.; ASTM D395; ISO 815
Tensile Set	10 %	10 %	ASTM D412
Torsional Stiffness	3.2383 MPa	469.68 psi	At 75°F (24°C); ASTM D1043
	27.56 MPa	3997 psi	At -4°F (-20°C); ASTM D1043

Thermal Properties	Metric	English	Comments
Brittleness Temperature	-86.1 °C	-123 °F	ASTM D746; ISO 812
Clash Berg Stiffness Temperature	-32.8 °C	-27.0 °F	At 10,000 psi (69 Mpa); ASTM D1043

Processing Properties	Metric	English	Comments
Processing Temperature	177 °C	350 °F

Descriptive Properties	Value	Comments
Fluid Resistance - Volume Change, % (ASTM D471)	31	After 7 Days in IRM 903 Oil No.3 at 212°F (100°C)
	32	After 7 Days in ASTM Ref. Fuel No. B at 75°F (24°C)
	5	After 7 Days in Water at 212°F (100°C)
	-8	After 7 Days in ASTM Oil No.1 at 212°F (100°C)