SABIC Innovative Plastics LNP STAT-KON TD000 PU
| Category | Polymer , Thermoplastic , Polyurethane, TP |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON TD000 PU.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STAT-KON* TD000 is an unfilled compound based on Polyurethane resin. Added feature of this material is: Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.26 g/cc | 1.26 g/cc | ASTM D792 |
| Density | 1.26 g/cc | 0.0455 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.500 % | 0.500 % | 50% RH, 24 hrs; ASTM D570 |
| 0.790 % | 0.790 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec |
>= 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 24.0 MPa | 3480 psi | 5 mm/min; ISO 527 |
| 25.0 MPa | 3630 psi | ASTM D638 | |
| Tensile Strength, Yield | 24.0 MPa | 3480 psi | 5 mm/min; ISO 527 |
| 26.0 MPa | 3770 psi | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Break | 140 % | 140 % | 5 mm/min; ISO 527 |
| 160 % | 160 % | ASTM D638 | |
| Elongation at Yield | 140 % | 140 % | 5 mm/min; ISO 527 |
| 160 % | 160 % | Type I, 50 mm/min; ASTM D638 | |
| Tensile Modulus | 0.180 GPa | 26.1 ksi | 50 mm/min; ASTM D638 |
| 0.300 GPa | 43.5 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 6.00 MPa | 870 psi | ASTM D790 |
| 16.0 MPa | 2320 psi | ISO 178 | |
| Flexural Modulus | 0.350 GPa | 50.8 ksi | 2 mm/min; ISO 178 |
| 0.360 GPa | 52.2 ksi | ASTM D790 | |
| Izod Impact, Notched | 7.94 J/cm | 14.9 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 10.03 J/cm | 18.79 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 78.0 kJ/m² | 37.1 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 87.0 kJ/m² | 41.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 50.0 J @Temperature 23.0 °C |
36.9 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 55.0 J | 40.6 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 12.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
6.67 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 14.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
7.78 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 69.0 °C | 156 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 70.0 °C @Thickness 3.20 mm |
158 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 48.0 °C | 118 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 47.0 °C @Thickness 3.20 mm |
117 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 10000 - 1.00e+6 ohm | 10000 - 1.00e+6 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycolac® MG47 ABS (Asia Pacific)
- Teknor Apex Telcar® OBC 2419A Thermoplastic Elastomer
- A. Schulman POLYBATCH™ Orange 1096 Concentrate Based In Polyethylene
- A. Schulman POLYBATCH™ White 8750 Concentrate Based In HDPE
- ChevronTexaco MCP Grease L NLGI Grade 00
- DuPont Teijin Films Mylar® A Polyester Film, 1000 Gauge
- Eurotec® Tecolen® CP20 GR40 NL PPCP, 40% glass fiber reinforced, natural
- Addiplast Addilene PMD 50213 Polypropylene Copolymer
Copyright © lookpolymers.com All Rights Reserved