UBE UBEPOL BR100 Non-Oil Extended Synthetic Rubber Vulcanizate (Cured 50 Minutes at 145°C)
| Category | Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE) |
| Manufacturer | UBE |
| Trade Name | UBEPOL |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | UBE UBEPOL BR100 Non-Oil Extended Synthetic Rubber Vulcanizate (Cured 50 Minutes at 145°C).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: UBEPOL BR is UBE's line of polybutadiene rubber products.Information provided by UBE.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 62 | 62 | ASTM D412 |
| Tensile Strength at Break | 17.9 MPa | 2600 psi | ASTM D412 |
| Elongation at Break | 490 % | 490 % | ASTM D412 |
| 100% Modulus | 0.00220 GPa | 0.319 ksi | ASTM D412 |
| 200% Modulus | 0.00530 GPa | 0.769 ksi | ASTM D412 |
| 300% Modulus | 0.0101 GPa | 1.46 ksi | ASTM D412 |
| Rebound | 57 % | 57 % | BS.903,PART22 |
| Tear Strength | 47.0 kN/m | 268 pli | ASTM D624 |
| Abrasion | 98 | 98 | Lombourn Abrasion Index (Iwamoto Seisakusyo, Japan); UBE Method |
| 202 | 202 | Pico Abrasion Index; ASTM D2228 | |
| Compression Set | 16 % | 16 % | Method B, 70°C, 72hrs; ASTM D395 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Cut Generation De Mattia Flexing Machine | Min 300,000 times | ASTM D430 |
| Cut Growth (2mm-->15mm) De Mattia Flexing Machine | 2400 times | ASTM D313 |
| Goodrich Flex, 0.175" Stroke, 55lb, 100°C, P.S. | 9% | ASTM D623 (33°C change in temperature) |
| Wet Skid Resistance on Safety-Walk | 18 | UBE Method (British Portable Skid Resistance Tester) |
Users viewing this material also viewed the following:
- Premix Thermoplastics PREBOARD E1025 Standard Epoxy Circuit Boards
- Chevron Phillips MA5350 HIPS - High Impact Polystyrene (discontinued **)
- SABIC Innovative Plastics Ultem 1010A PEI (Europe-Africa-Middle East)
- SMAC CABLE® 2515S-30-10 Damping Material
- TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, Hardness 70A
- Chevron Phillips Marlex® M248 LLDPE Carbon Black Concentrate
- Beijing Ranger Chem E-21 Solid Epoxy Resin
- Aremco Lamp-Coat™ LC4040-SG High Temperature Coating, Silicone
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 120 PHR N650 Filler
- NOVA Chemicals Novapol® LF-0218-AF LDPE Extrusion Resin (discontinued **)
Copyright © lookpolymers.com All Rights Reserved