SABIC Innovative Plastics LNP STAT-KON RE006 PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON RE006 PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP STAT-KON* RE006 is a compound based on Nylon 66 resin containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.27 g/cc | 1.27 g/cc | ASTM D792 |
| Density | 1.27 g/cc | 0.0459 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.720 % | 0.720 % | 50% RH, 24 hrs; ASTM D570 |
| 1.10 % | 1.10 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0080 - 0.010 cm/cm @Time 86400 sec |
0.0080 - 0.010 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 238 MPa | 34500 psi | 5 mm/min; ISO 527 |
| 246 MPa | 35700 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.3 % | 2.3 % | 5 mm/min; ISO 527 |
| 2.5 % | 2.5 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 20.33 GPa | 2949 ksi | 1 mm/min; ISO 527 |
| 22.2 GPa | 3220 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 268 MPa | 38900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 355 MPa | 51500 psi | ISO 178 | |
| Flexural Yield Strength | 368 MPa | 53400 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 16.95 GPa | 2458 ksi | 2 mm/min; ISO 178 |
| 17.6 GPa | 2550 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 1.19 J/cm | 2.23 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 10.3 J/cm | 19.3 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 61.0 kJ/m² | 29.0 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 9.00 J @Temperature 23.0 °C |
6.64 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 33.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
18.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 48.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
26.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 259 °C | 498 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 261 °C @Thickness 3.20 mm |
502 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 248 °C | 478 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 255 °C @Thickness 3.20 mm |
491 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 100 ohm - 1e+05 | 100 ohm - 1e+05 | ASTM D257 |
Users viewing this material also viewed the following:
- Polikim ULPOLEN® 300 UHMWPE Standard
- SABIC Innovative Plastics Lexan® CFR9131 PC COPOLYMER
- Lanxess Pocan® B 7375 000000 PBT, White Pigment
- SK Chemicals SKYTHANE® 168D S series Polyurethane
- Teknor Apex Monprene® MP-2870UV Thermoplastic Elastomer
- DuPont Performance Polymers Zytel® 77G43L NC010 Nylon 612 (Unverified Data**)
- Asahi Kasei Thermylene® P6-30FG-0708 30% Glass Fiber Reinforced, High Impact
- Arlon 51581B015 0.015" Uncured Silicone Rubber with Fiberglass Substrate
- 3M 8902 Polyester Tape
- A. Schulman POLYBATCH™ White LL8350 AP Concentrate Based In LLDPE
Copyright © lookpolymers.com All Rights Reserved