SABIC Innovative Plastics LNP STAT-KON OE004AE PPS - Branched
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON OE004AE PPS - Branched.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP STAT-KON* OE004AE is a compound based on PPS - Branched resin containing 20% Carbon Fiber. Added features of this material are: Easy Molding, Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | ASTM D792 |
| 1.42 g/cc | 0.0513 lb/in³ | ISO 1183 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0070 cm/cm @Time 86400 sec |
0.0050 - 0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 146 MPa | 21200 psi | 5 mm/min; ISO 527 |
| 163 MPa | 23600 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 146 MPa | 21200 psi | 5 mm/min; ISO 527 |
| 163 MPa | 23600 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 0.80 % | 0.80 % | Type I, 5 mm/min; ASTM D638 |
| 0.80 % | 0.80 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 0.80 % | 0.80 % | Type I, 5 mm/min; ASTM D638 |
| 0.80 % | 0.80 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 19.12 GPa | 2773 ksi | 1 mm/min; ISO 527 |
| 27.16 GPa | 3939 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 215 MPa | 31200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Yield Strength | 208 MPa | 30200 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 15.71 GPa | 2279 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 16.05 GPa | 2328 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.470 J/cm | 0.881 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.54 J/cm | 4.76 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 279 °C @Thickness 3.20 mm |
534 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 262 °C | 504 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 263 °C @Thickness 3.20 mm |
505 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 100 - 1.00e+6 ohm | 100 - 1.00e+6 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Nylene® 451 Nylon 6, 50% RH
- Rogers Corporation RO3003 Ceramic-Filled PTFE Composite, High Frequency Circuit Material
- S&E Specialty Polymers TufFill NH™ GTPO8290-36 TPO
- LATI Laril 13 G/10-V1 PPOm, 10% Glass Fiber Reinforced, Flame Retardant
- Sylvin Technologies 9600-80 Clear PVC Molding Compound
- CLAL-MSX ARCAP Anticorrosion AP4 H12 1/2 hard, Rolled Copper Alloy
- Arlon 920-10C##FR-P0 0.020" (0.508 mm) Cured Self-fusing Silicone Tape
- A. Schulman ComAlloy Voloy® 431 Glass/Mineral Reinforced, PET Alloy, Flame Retardant, UL
- Axiall 830B Wire & Cable Flexible PVC
- 3M OFM0102 Outdoor UL Recognized Polyester Overlaminate Label Products
Copyright © lookpolymers.com All Rights Reserved